Advanced fire-resistant forms of activated carbon and methods of adsorbing and separating gases using same
View Patent ↗A method of removing a target gas from a gas stream is disclosed. The method uses advanced, fire-resistant activated carbon compositions having vastly improved fire resistance. Methods for synthesizing the compositions are also provided. The advanced compositions have high gas adsorption capacities and rapid adsorption kinetics (comparable to commercially-available activated carbon), without having any intrinsic fire hazard.
1. A method of removing a target gas from a gas stream comprising contacting a gas stream comprising a target gas with an advanced activated carbon composition, the composition selected from a group consisting of: activated carbon and between 15 and 40 wt % hydrated magnesite; activated carbon and between 30 and 50 wt % hydrated sepiolite; activated carbon and between 30 and 45 wt % hydrated nesquehonite; activated carbon and between 45 and 60 wt % hydrated calcium citrate tribasic; and any combination thereof.
2. The method of claim 1 , wherein the contacting occurs at a temperature between room temperature and a minimum ignition temperature of the advanced activated carbon.
3. The method of claim 1 , wherein structural water and/or CO 2 is released from the advanced activated carbon during contacting.
4. The method of claim 1 , wherein the target gas is selected from the group of noble gases, 129 I gas, volatile organic compounds, and combinations thereof.
5. The method of claim 1 , wherein the gas stream comprises a mixture of krypton and argon, and the target gas is krypton.
6. The method of claim 1 , wherein the advanced activated carbon composition has a K Kr /K ar gas adsorption selectivity ratio greater than or equal to 8.
7. The method of claim 1 , wherein the advanced activated carbon composition has a spontaneous ignition temperature greater than or equal to 500° C.
8. A method of synthesizing an advanced activated carbon composition, the method comprising performing a chemical precipitation mixing, in the following proportions and in the following order:
a) making a slurry by combining a pre-measured amount of activated carbon with an aqueous solution of Na 2 CO 3 in a beaker and stirring; then
b) adding MgCl 2 to the slurry and stirring, thereby precipitating hydromagnesite; then
c) filtering out solids from the slurry after hydromagnesite has precipitated and drying said solids; then finally
d) grinding the dried solids to less than 1 micron particle size.