Porous polyurethane networks and methods of preparation
Nanoporous three-dimensional networks of polyurethane particles, e.g., polyurethane aerogels, and methods of preparation are presented herein. Such nanoporous networks may include polyurethane particles made up of linked polyisocyanate and polyol monomers. In some cases, greater than about 95% of the linkages between the polyisocyanate monomers and the polyol monomers are urethane linkages. To prepare such networks, a mixture including polyisocyanate monomers (e.g., diisocyanates, triisocyanates), polyol monomers (diols, triols), and a solvent is provided. The polyisocyanate and polyol monomers may be aliphatic or aromatic. A polyurethane catalyst is added to the mixture causing formation of linkages between the polyisocyanate monomers and the polyol monomers. Phase separation of particles from the reaction medium can be controlled to enable formation of polyurethane networks with desirable nanomorphologies, specific surface area, and mechanical properties. Various properties of such networks of polyurethane particles (e.g., strength, stiffness, flexibility, thermal conductivity) may be tailored depending on which monomers are provided in the reaction.
1. A composition comprising:
a porous solid-phase three-dimensional network of polyurethane particles, the particles comprising linked polyisocyanate and polyol monomers, wherein:
greater than about 95% of linkages between the polyisocyanate and polyol monomers are urethane linkages, and
the porous solid-phase three-dimensional network of polyurethane particles is flexible.
2. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles is configured such that a 0.4-inch thick sample of the porous solid-phase three-dimensional network can be deformed such that a surface of the sample forms a 0.9-inch radius of curvature.
3. The composition of claim 1 , wherein the particles comprise linked triisocyanate and polyol monomers.
4. The composition of claim 1 , wherein the particles comprise linked polyisocyanate and saccharide monomers.
5. The composition of claim 1 , wherein the particles comprise linked triisocyanate and saccharide monomers.
6. The composition of claim 1 , wherein the particles comprise linked tris(isocyanatophenyl)methane and pentaerythritol monomers.
7. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles is stable at 300° C.
8. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles does not burn at any temperature below 300° C.
9. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles has a Young's modulus of 15 MPa or less.
10. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles has a Young's modulus of from 1.0 MPa to 15 MPa.
11. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles has a Young's modulus of 8.7 MPa or less.
12. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles has a Young's modulus of from 1.0 MPa to 8.7 MPa.
13. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles has a Young's modulus of 3.0 MPa or less.
14. The composition of claim 1 , wherein the porous solid-phase three-dimensional network of polyurethane particles has a Young's modulus of from 1.0 MPa to 3.0 MPa.