Precursor for preparing lithium composite transition metal oxide, method for preparing the precursor, and lithium composite transition metal oxide
View Patent ↗Disclosed are a transition metal precursor for preparing a lithium composite transition metal oxide, a method for preparing the precursor, and a lithium composite transition metal oxide. The transition metal precursor includes a composite transition metal compound having a composition represented by Formula (1) and a Mn content of 60 to 85 mol %: Ni a M b Mn 1-(a+b) (OH 1-x ) 2 (1) where M is at least one selected from the group consisting of Ti, Co, Al, Cu, Fe, Mg, B, Cr, Zr, Zn and period II transition metals, 0.15≤a≤0.3, 0≤b≤0.1 and 0<x<0.5. The lithium composite transition metal oxide has a composition represented by Formula (2) and a Mn content of 60 to 85 mol %: Li 1+z [Ni a M b Mn 1-(a+b) ] 2 O 4-y A y (2) where M is at least one selected from the group consisting of Ti, Co, Al, Cu, Fe, Mg, B, Cr and period II transition metals, A is a monoanion or dianion, 0.15≤a≤0.3, 0.005≤b≤0.1, −0.1≤z≤0.1 and 0≤y≤0.1.
1. A transition metal precursor comprising a composite transition metal compound having a composition represented by Formula (1) and a Mn content of 60 to 85 mol %:
Ni a M b Mn 1-(a+b) (H 1-x ) 2 (1)
where M is at least one selected from the group consisting of Ti, Co, Al, Cu, Fe, Mg, B, and Cr,
0.15≤a≤0.3,
0≤b≤0.1, and
0<x<0.5; and
a saccharide material present on the surface and/or inside of the transition metal precursor wherein at least part of the saccharide material is present in a closed pore formed in the metal transition precursor, and wherein a tap density of the composite transition metal compound is 0.8 to 2.5 g/cm 3 .
2. The transition metal precursor according to claim 1 , wherein M is Ti or Al.
3. The transition metal precursor according to claim 1 , wherein a is equal to or greater than 0.2 and equal to or less than 0.25.
4. The transition metal precursor according to claim 1 , wherein the Mn content is 70 to 80 mol %.
5. The transition metal precursor according to claim 1 , wherein x is equal to or greater than 0.2 and less than 0.5.
6. The transition metal precursor according to claim 1 , wherein x is equal to or greater than 0.3 and less than 0.5.
7. The transition metal precursor according to claim 1 , wherein an average particle diameter of the composite transition metal compound is 4 to 20 micrometers.
8. The transition metal precursor according to claim 1 , wherein the composite transition metal compound is prepared by coprecipitation in a state in which a basic substance and the saccharide material for preventing oxidation of Mn are added to an aqueous transition metal solution mixed with a transition metal-containing salt.
9. The transition metal precursor according to claim 8 , wherein the saccharide material is added in an amount of 0.01 to 10 mol % relative to the molar quantity of the aqueous transition metal solution.
10. The transition metal precursor according to claim 8 , wherein the transition metal-containing salt comprises sulfate and the basic material comprises sodium hydroxide.
11. The transition metal precursor according to claim 10 , wherein the sulfate comprises at least one selected from the group consisting of nickel sulfate, titanium sulfate and manganese sulfate.
12. The transition metal precursor according to claim 1 , wherein the saccharide material comprises at least one selected from the group consisting of fructose, sucrose, glucose, galactose, lactose, maltose, starch and dextrin.
13. The transition metal precursor according to claim 1 , wherein the saccharide material comprises sucrose.
14. The transition metal precursor according to claim 1 , wherein the content of the composite transition metal compound is 30% by weight or higher, based on the total amount of the transition metal precursor.
15. The transition metal precursor according to claim 14 , wherein the content of the composite transition metal compound is 50% by weight or higher.
16. A method for preparing the composite transition metal compound of the transition metal precursor according to claim 1 , the method comprising:
(i) preparing an aqueous transition metal solution containing a transition metal salt for precursor preparation;
(ii) mixing, with the aqueous transition metal solution, 0.01 to 10 mol % of a reductant relative to the molar quantity of the aqueous transition metal solution; and
(iii) adding a strong base to the aqueous transition metal solution mixed with the reductant to induce coprecipitation.