Method of hardening articles and articles comprising the same
View Patent ↗Disclosed herein is a method comprising disposing on a base article a nickel-titanium alloy; where the nickel is in an amount of about 58 to about 62 weight percent and titanium in an amount of about 38 to about 42 wt %, based on the total weight of the nickel-titanium alloy; and applying a pressure of 12 to 20 kilopounds per square inch at a temperature of 1400 to 2100° F. for a period of 1 to 8 hours to form a nickel-titanium alloy coating on the base article. Disclosed is an article comprising a base article; and a nickel-titanium alloy; where the nickel-titanium alloy is disposed on the base article; where the nickel is in an amount of about 58 to about 62 weight percent and titanium in an amount of about 38 to about 42 wt %, based on the total weight of the nickel-titanium alloy.
1. A method comprising:
disposing on an outer surface of a base article a nickel-titanium alloy; wherein the nickel is in an amount of about 58 to about 62 weight percent and titanium in an amount of about 38 to about 42 wt %, each based on the total weight of the nickel-titanium alloy;
hermetically sealing a can under vacuum, wherein the nickel-titanium alloy is in the form of a loose powder and is disposed between the outer surface of the base article and an inner surface of the hermetically sealed can; and
applying a pressure of 12 to 20 kilopounds per square inch at a temperature of 1400 to 2100° F. for a period of 1 to 8 hours to the hermetically sealed can to form a nickel-titanium alloy coating on the base article.
2. The method of claim 1 , wherein the base article comprises a metal, an intermetallic compound or a ceramic.
3. The method of claim 1 , further comprising disposing the base article and the nickel-titanium alloy in the can.
4. The method of claim 1 , further comprising removing the can after the applying of the pressure.
5. The method of claim 1 , wherein a surface hardness of the nickel-titanium alloy coating on the base article is 40 to 62 Rockwell.
6. The method of claim 2 , wherein the base article comprises a metal, an intermetallic compound or a ceramic.
7. An article comprising:
a base article comprising an outer surface;
a nickel-titanium alloy disposed on the outer surface of the base article; and
a hermetically sealed can under vacuum containing the nickel-titanium alloy and the base article,
wherein the nickel-titanium alloy is in the form of a loose powder and is disposed between the outer surface of the base article and an inner surface of the hermetically sealed can, and
wherein the nickel is in an amount of about 58 to about 62 weight percent and titanium is in an amount of about 38 to about 42 weight percent, each based on the total weight of the nickel-titanium alloy.
8. The article of claim 7 , wherein the base article comprises a metal, an intermetallic compound, or a ceramic.
9. The article of claim 7 , wherein the outer surface of the base article is textured prior to a deposition of the nickel-titanium alloy.
10. The article of claim 7 , further comprising a coating disposed between the base article and the nickel-titanium alloy.
11. The article of claim 7 , wherein the hermetically sealed can comprises mild steel.
12. The article of claim 7 , wherein the hermetically sealed can is under a vacuum of 1×10 −1 to 1×10 −5 Torr.