Method of manufacturing carbon nanotubes and fibers using catalytic magnesium oxide nanoparticles
View Patent ↗A method for producing carbon nanotubes and/or fibers, such as carbon nano-tubes, involves sparging a gas (such as carbon dioxide) through a liquid hydrocarbon (such as crude oil) in the presence of an effective amount of magnesium oxide (MgO) particles (such as MgO nanoparticles having a size in the range from about 2 nm to about 10 microns, and which may have a bimodal particle size distribution) at a temperature in a range of between about 70 to about 90° C. to produce carbon nanotubes and fibers having a size range of from about 50 nm to about 20 microns.
1. A method for producing carbon nanotubes and/or carbon fibers comprising:
sparging a gas through a liquid hydrocarbon in the presence of an effective amount of magnesium oxide particles at a temperature in a range of between about 70 to about 90° C. to produce carbon nanotubes and/or fibers.
2. The method of claim 1 where the gas is selected from the group consisting of carbon dioxide, argon, and mixtures thereof.
3. The method of claim 1 where the liquid hydrocarbon is crude oil.
4. The method of claim 1 where the effective amount of magnesium oxide particles concentration ranges from 50 ppm to 10 wt % MgO.
5. The method of claim 1 where the magnesium oxide particles have a particle size range of from about 2 nanometers to about 10 microns.
6. The method of claim 1 where the magnesium oxide particles are present in a bimodal particle size distribution where the magnesium oxide particles have an average particle size between about 90 nm to about 5 microns, where the amount of the magnesium oxide particles of a size less than 1000 nm is more than the amount of magnesium oxide particles of a size of 1 micron or greater.
7. The method of claim 1 where the amount of gas sparged through the liquid hydrocarbon based on the liquid hydrocarbon ranges from about 0.1 to about 10 volume %.
8. The method of claim 1 where the sizes of the carbon nanotubes and/or carbon fibers range from about 50 nm to about 20 microns.
9. A method for producing carbon nanotubes and/or carbon fibers comprising:
sparging carbon dioxide gas through a liquid hydrocarbon in the presence of from about 10 to about 500,000 ppm of magnesium oxide particles, based on the liquid hydrocarbon, at a temperature in a range of between about 70 to about 90° C. to produce carbon nanotubes and/or fibers.
10. The method of claim 9 where the liquid hydrocarbon is crude oil.
11. The method of claim 9 where the magnesium oxide particles have a particle size range of from about 2 nanometers to about 10 microns.
12. The method of claim 9 where the magnesium oxide particles are present in a bimodal particle size distribution where the magnesium oxide particles have an average particle size between about 90 nm to about 5 microns, where the amount of the magnesium oxide particles of a size less than 1000 nm is more than the amount of magnesium oxide particles of a size of 1 micron or greater.
13. The method of claim 9 where the amount of gas sparged through the liquid hydrocarbon based on the liquid hydrocarbon ranges from about 0.1 to about 10 volume %.
14. The method of claim 9 where the sizes of the carbon tubes and/or carbon fibers range from about 50 nm to about 20 microns.
15. The method of claim 9 where the amount of nanoparticles present range from about 50 to about 1000 ppm, based on the liquid hydrocarbon.
16. A method for producing carbon nanotubes and/or carbon fibers comprising:
sparging carbon dioxide gas through a liquid crude oil in the presence of from about 10 to about 500,000 ppm of magnesium oxide particles, based on the liquid crude oil, at a temperature in a range of between about 70 to about 90° C. to produce carbon nanotubes and/or carbon fibers, where the magnesium oxide particles have a particle size range of from about 2 nanometers to about 10 microns, where the amount of gas sparged through the liquid crude oil based on the liquid crude oil ranges from about 0.1 to about 10 volume %.
17. The method of claim 16 where the magnesium oxide particles are present in a bimodal particle size distribution where the magnesium oxide particles have an average particle size between about 90 nm to about 5 microns, where the amount of the magnesium oxide particles of a size less than 1000 nm is more than the amount of magnesium oxide particles of a size of 1 micron or greater.
18. The method of claim 16 where the amount of nanoparticles present range from about 50 to about 1000 ppm.
19. The method of claim 16 where the sizes of the carbon nanotubes and/or carbon fibers range from about 50 nm to about 20 microns.