Amorphous propylene-ethylene copolymers
View Patent ↗Amorphous propylene-ethylene copolymers are described herein that can include high amounts of ethylene and exhibit desirable softening points and needle penetrations. The desirable combinations of softening points and needle penetrations in these propylene-ethylene copolymers allow them to have a broad operating window. Due their broad operating window, the propylene-ethylene copolymers can be utilized in a wide array of applications and products, including hot melt adhesives.
1. A process for producing a copolymer, said process comprising:
reacting propylene and ethylene in the presence of a catalyst system comprising an electron donor to form said copolymer,
wherein said copolymer has a softening point in the range of 90 to 140° C.,
wherein said copolymer has a needle penetration that is equal to y,
wherein y is defined by the following formula:
y≦− 0.000000262249 x 6 +0.000172031278 x 5 −0.046669720165 x 4 +6.701746779438 x 3 −537.286013331959 x 2 +22,802.983472587 x− 400,204.018086126
wherein x in the above formula is the softening point of said copolymer;
wherein said electron donor comprises an alkyloxy silane; and
wherein said catalyst system has a molar ratio of aluminum to silicon in the range of 1:1 to 100.
2. The process of claim 1 , wherein said alkoxy silane comprises dicyclopentyldimethoxysilane or cyclohexylmethyldimethoxysilane.
3. The process of claim 1 , wherein said catalyst system comprises an alkyl aluminum co-catalyst, wherein said catalyst system comprises a molar ratio of said alkyl aluminum co-catalyst to said electron donor in the range of 1:1 to 50:1.
4. The process of claim 1 , wherein said needle penetration is in the range of 10 to 30 dmm.
5. The process of claim 1 , wherein the weight ratio of propylene to ethylene in said copolymer is in the range of 1:1 to 5:1.