Method of manufacturing solar cell module and solar cell module
View Patent ↗A stack is obtained by stacking a glass plate, a first transparent resin sheet, a solar cell, a second transparent resin sheet, a colored resin sheet, and a first resin sheet. The stack is pressed under heat to fabricate a module including the glass plate, a first transparent bonding layer placed between the glass plate and the solar cell and formed of the first transparent resin sheet, a second transparent bonding layer placed between the first resin sheet and the solar cell and formed of the second transparent resin sheet, a colored bonding layer placed between the second transparent bonding layer and the first resin sheet and formed of the colored resin sheet, and the first resin sheet. A loss modulus of the colored resin sheet at a temperature of the pressing is higher than a loss modulus of the first transparent resin sheet at the temperature of the pressing.
1. A method of manufacturing a solar cell module, the method comprising:
obtaining a stack by stacking a glass plate, a first transparent resin sheet, a solar cell, a second transparent resin sheet, a colored resin sheet, and a first resin sheet in the order mentioned; and
pressing the stack under heat to fabricate the solar cell module including
the glass plate,
a first transparent bonding layer placed between the glass plate and the solar cell and formed of the first transparent resin sheet,
a second transparent bonding layer placed between the first resin sheet and the solar cell and formed of the second transparent resin sheet,
a colored bonding layer placed between the second transparent bonding layer and the first resin sheet and formed of the colored resin sheet, and
the first resin sheet, wherein
a loss modulus of the colored resin sheet at a temperature of the pressing is higher than a loss modulus of the first transparent resin sheet at the temperature of the pressing, and wherein
the loss modulus of the colored bonding layer at 125 degrees C. is three times or more the loss modulus of the first transparent bonding layer at 125 degrees C.
2. The method of manufacturing a solar cell module according to claim 1 , wherein
the loss modulus of the colored resin sheet at the temperature of the pressing is four times or more the loss modulus of the first transparent resin sheet at the temperature of the pressing.
3. The method of manufacturing a solar cell module according to claim 1 , wherein
the loss modulus of the colored resin sheet at the temperature of the pressing is 300,000 Pa or higher.
4. The method of manufacturing a solar cell module according to claim 1 , wherein
the loss modulus of the first transparent resin sheet at the temperature of the pressing is 200,000 Pa or less.
5. The method of manufacturing a solar cell module according to claim 1 , wherein
a loss modulus of the second transparent resin sheet at the temperature of the pressing is higher than the loss modulus of the first transparent resin sheet at the temperature of the pressing.
6. The method of manufacturing a solar cell module according to claim 5 , wherein
the loss modulus of the second transparent resin sheet at the temperature of the pressing is 300,000 Pa or higher.
7. The method of manufacturing a solar cell module according to claim 1 , wherein
the first resin sheet is made of resin.
8. The method of manufacturing a solar cell module according to claim 1 , wherein the temperature of the pressing is 100 degrees to 160 degrees C.