Metal-backed plain bearing
View Patent ↗A bearing comprises a resin matrix filled with fluoropolymer, graphite, and other discrete particles of an additive material that is attached to a backing material. A method for manufacturing a bearing comprises depositing to a backing material a fluid polymer bearing material comprised of a resin matrix filled with fluoropolymer, various fillers, and discrete particles of an additive to form a continuous consolidated bearing material, and curing the lining material to bond the lining material onto the backing material.
1. A method for forming a plain bearing, comprising:
providing a single layer metal substrate;
leveling the single layer metal substrate to form a backing material;
preparing a bearing lining material comprising a mixture of approximately 70 to 90% by volume of an epoxide thermoset resin, approximately 5 to 20% by volume of at least one fluoropolymer, and approximately 1 to 8% by volume of at least one other filler;
depositing the bearing lining material directly onto the single layer metal substrate; and
drying the bearing lining material to bond the bearing lining material directly onto the single layer metal substrate and to form a bearing lining material layer having a constant thickness; wherein the bearing lining material deposited directly onto the single layer metal substrate is free of solvent.
2. The method of claim 1 , wherein the single layer metal substrate is a metal sheet in coil form, and wherein leveling comprises leveling by a straightening machine to form the backing material.
3. The method of claim 1 , wherein the fluoropolymer comprises approximately 12% by volume of PTFE.
4. The method of claim 1 , wherein the at least one other filler comprises approximately 2% by volume of graphite.
5. The method of claim 1 , wherein the at least one fluoropolymer comprises PTFE.
6. The method of claim 1 , wherein the at least one other filler comprises graphite.
7. The method claim 1 , wherein the single layer metal substrate is placed on a vacuum table after being leveled and prior to depositing bearing lining material thereon.
8. The method of claim 1 , wherein the method further comprises:
leveling the bearing lining material after depositing the bearing lining material on the single layer metal substrate and prior to drying the bearing lining material.
9. The method of claim 1 , wherein depositing the bearing lining material directly onto the single layer metal substrate comprises depositing the bearing lining material in an amount such that multiple layers of the at least one fluoropolymer and the at least one other filler are provided within the bearing lining material.
10. A method for forming a plain bearing, comprising:
preparing a bearing lining material comprising a mixture of approximately 70 to 90% by volume of an epoxide thermoset resin, approximately 5 to 20% by volume of at least one fluoropolymer, and approximately 1 to 8% by volume of at least one other filler;
depositing the bearing lining material directly onto a single layer metal substrate; and
drying the bearing lining material to bond the bearing lining material directly onto the single layer metal substrate and to form a bearing lining material layer having a constant thickness; wherein the bearing lining material deposited directly onto the single layer metal substrate is free of solvent.
11. The method of claim 10 , wherein the fluoropolymer comprises approximately 12% by volume of PTFE.
12. The method of claim 10 , wherein the at least one other filler comprises approximately 2% by volume of graphite.
13. The method of claim 10 , wherein the at least one fluoropolymer comprises PTFE.
14. The method of claim 10 , wherein the at least one other filler comprises graphite.
15. The method claim 10 , wherein the single layer metal substrate is placed on a vacuum table prior to depositing bearing lining material thereon.
16. The method of claim 10 , wherein the method further comprises:
leveling the bearing lining material after depositing the bearing lining material on the single layer metal substrate and prior to drying the bearing lining material.
17. The method of claim 10 , wherein depositing the bearing lining material directly onto the single layer metal substrate comprises depositing the bearing lining material in an amount such that multiple layers of the at least one fluoropolymer and the at least one other filler are provided within the bearing lining material.