Process for the preparation of an edible dispersion comprising oil and structuring agent
The invention relates to a process for the preparation of an edible dispersion comprising oil and structuring agent and one or more of an aqueous phase and/or a solid phase, in which the dispersion is formed by mixing oil, solid structuring agent particles and the aqueous phase and/or the solid phase, wherein the solid structuring agent particles have a microporous structure of submicron size particles.
1. A process for the preparation of an edible dispersion comprising a) oil and structuring agent and b) an aqueous phase, comprising:
a) preparing solid structuring agent particles comprising edible fat, and having a microporous structure of submicron size particles, by
preparing a homogeneous mixture of A) structuring agent and B) liquefied gas or supercritical gas, at a pressure of 5-40 MPa, and
expanding the mixture through an orifice, in which the structuring agent is solidified; and
b) forming the edible dispersion by mixing i) the oil, ii) the solid structuring agent particles, and iii) the aqueous phase,
wherein said edible dispersion comprises a water-in-oil emulsion.
2. The process of claim 1 , wherein the solid structuring agent particles are at least 50% alpha-polymorph.
3. The process of claim 1 , wherein the solid structuring agent particles have an average diameter D 3,2 of 60 μm or lower.
4. The process of claim 1 , wherein the homogenized mixture comprises oil.
5. The process of claim 1 , wherein the temperature of the mixture of structuring agent and liquefied gas or supercritical gas is below the slip melting point of the structuring agent at atmospheric pressure and above the temperature at which phase separation of the mixture occurs.
6. The process of claim 1 , wherein the mixture is expanded through the orifice under conditions that a spay jet is applied and wherein a gas jet is applied in addition to the spray jet.
7. The process of claim 1 , wherein the gas comprises carbon dioxide.
8. The process of claim 1 , wherein the pressure is within the range of 15-40 MPa.
9. The process of claim 1 , wherein in the course of preparation of the dispersion the microporous structure is broken into submicron particles.
10. A process for the preparation of an edible dispersion comprising (a) oil and structuring agent and (b) one or more of an aqueous phase and/or a solid phase, comprising:
a) preparing solid structuring agent particles having a microporous structure of submicron size particles by
preparing a homogeneous mixture of (A) structuring agent and (B) liquefied gas or supercritical gas at a pressure of 5-40 MPa,
expanding the mixture through an orifice, in which the structuring agent is solidified; and
b) forming the edible dispersion by mixing (i) the oil, (ii) the solid structuring agent particles, and (iii) the aqueous phase and/or the solid phase, wherein the edible dispersion is an emulsion and wherein in the course of preparing the edible dispersion the microporous structure of the solid structuring agent particles is broken into submicron particles.
11. The process of claim 10 , wherein the gas comprises carbon dioxide.
12. The process of claim 1 , wherein the solid structuring agent particles are at least 90% alpha-polymorph.
13. The process of claim 1 , wherein the solid structuring agent particles are 100% alpha-polymorph.
14. The process of claim 1 , wherein the solid structuring agent particles are not heated above the melting point of the solid structuring agent during steps a) or b).