Method for manufacturing a metallic or ceramic component by selective laser melting additive manufacturing
View Patent ↗The invention refers to a method for selective laser melting additive manufacturing a three-dimensional metallic or ceramic article/component entirely or partly. The method includes successively building up said article/component layer by layer directly from a powder bed of a metallic or ceramic base material by means of remelting the layers with a high energy laser beam, moving repetitively across the areas, which are to be solidified. The movement of the laser beam is made of a superposition of a continuous linear movement and at least one superimposed oscillation with a determined frequency and amplitude. The oscillation is created by a beam deflection device and the same beam deflection device is also used for linear positioning movement.
1. A method for selective laser melting additive manufacturing a three-dimensional article/component entirely or partly, the method comprising:
successively building up an article/component layer-by-layer directly from a powder bed of a base material by remelting the layers with a high energy laser beam; and
moving repetitively across the areas which are to be solidified, wherein the movement of the laser beam on a surface of the powder bed is made of a superposition of a continuous linear movement and at least one superimposed sinusoidal oscillation with a frequency and an amplitude, wherein the oscillation is created by a beam deflection device and the same beam deflection device which is also used for linear positioning movement, wherein a lateral offset between adjacent axes of the linear movement of the laser beam across the surface of the powder bed equals 0.5-3× the amplitude of the oscillation.
2. The method according to claim 1 , wherein an oscillation frequency is in a range from 10 to 50 000 Hz.
3. The method according to claim 1 , wherein an oscillation amplitude is in a range from 0.01 mm to 20 mm.
4. The method according to claim 1 , wherein oscillation parameters, of frequency and amplitude, and a linear movement parameter, are adjusted such that linear displacement of the laser beam during one oscillation half period is in a range from 0.01 to 2.0 times of a beam diameter at a top surface of the powder bed.
5. The method according to claim 1 , wherein the power bed is a metallic material.
6. The method according to claim 5 , wherein said metallic material is one of a high-temperature Ni-based alloy, Co-based alloy, Fe-based alloy or combinations thereof.
7. The method according to claim 6 , wherein said alloy contains finely dispersed oxides of one of Y2O3, Al2O3, ThO2, HfO2, ZrO2.
8. The method according to claim 1 , wherein the power bed is a ceramic material.
9. A method for selective laser melting additive manufacturing a three-dimensional article/component entirely or partly, the method comprising:
successively building up an article/component layer-by-layer directly from a powder bed of a base material by remelting the layers with a high energy laser beam; and
moving repetitively across the areas which are to be solidified, wherein the movement of the laser beam on a surface of the powder bed is made of a superposition of a continuous linear movement and at least one superimposed sinusoidal oscillation with a frequency and an amplitude, wherein the oscillation is created by a beam deflection device and the same beam deflection device which is also used for linear positioning movement, wherein oscillation parameters, of frequency and amplitude, and a linear movement parameter, are adjusted such that linear displacement of the laser beam during one oscillation half period is in a range from 0.01 to 2.0 times of a beam diameter at a top surface of the powder bed.
10. The method according to claim 9 , wherein an oscillation frequency is in a range from 10 to 50 000 Hz.
11. The method according to claim 9 , wherein an oscillation amplitude is in a range from 0.01 mm to 20 mm.
12. The method according to claim 9 , wherein the power bed is a metallic material.
13. The method according to claim 12 , wherein said metallic material is one of a high-temperature Ni-based alloy, Co-based alloy, Fe-based alloy or combinations thereof.
14. The method according to claim 13 , wherein said alloy contains finely dispersed oxides of one of Y2O3, Al2O3, ThO2, HfO2, ZrO2.
15. A method for selective laser melting additive manufacturing a three-dimensional article/component entirely or partly, the method comprising:
successively building up an article/component layer-by-layer directly from a powder bed of a base material by remelting the layers with a high energy laser beam; and
moving repetitively across the areas which are to be solidified, wherein the movement of the laser beam on a surface of the powder bed is made of a superposition of a continuous linear movement and at least one superimposed sinusoidal oscillation with a frequency and an amplitude, wherein the oscillation is created by a beam deflection device and the same beam deflection device which is also used for linear positioning movement, wherein the power bed is one of a high-temperature Ni-based alloy, Co-based alloy, Fe-based alloy or combinations thereof, and said alloy contains finely dispersed oxides of one of Y2O3, Al2O3, ThO2, HfO2, ZrO2.
16. The method according to claim 15 , wherein an oscillation frequency is in a range from 10 to 50 000 Hz.
17. The method according to claim 15 , wherein an oscillation amplitude is in a range from 0.01 mm to 20 mm.