Lead-bismuth-tellurium-silicate inorganic reaction system having improved adhesion properties
View Patent ↗An inorganic reaction system comprising a lead-bismuth-tellurium-silicate composition of Formula (I): Pb a —Bi b —Te c —Si g -M d -O e , wherein 0<a, b, c, d, or g≤1, 0≤d, e≤1, and the sum of a, b, c, d and g is 1, 0<a≤0.05, 0.2<b≤0.95, 0<c≤0.5, 0<d≤0.2, 0<g≤0.5, a:b is between about 0.1:99.9 to about 5:95, b:c is between about 50:50 to 99:1, a:c is between about 1:99 to about 10:90, b:g is between about 50:50 to about 98:2, M is one or more elements, and e is a number sufficient to balance the Pb, Bi, Te, Si, and M components.
1. An electroconductive paste comprising:
metallic particles;
at least one inorganic reaction system comprising a lead-bismuth-tellurium-silicate composition of Formula (I):
Pb a —Bi b —Te c —Si g -M d -O e , (I)
wherein
the sum of a, b, c, d and g is 1,
0<a≤0.01,
0.2<b≤0.95,
0≤c≤0.5,
0<d≤0.2,
0<g≤0.5,
a:b is between about 0.1:99.9 to about 5:95,
b:c is between about 50:50 to 99:1,
a:c is between about 1:99 to about 10:90,
b:g is between about 50:50 to about 98:2,
M is one or more elements selected from the group consisting of boron, aluminum, gallium, germanium, tin, phosphorus, antimony, niobium, tantalum, vanadium, titanium, molybdenum, tungsten, chromium, silver, halides, chalcogenides, alkaline metals, alkaline earth metals, and rare earth metals, and
e is a number sufficient to balance the charge of the Pb, Bi, Te, Si, and M components; and
an organic vehicle.
2. The inorganic reaction system according to claim 1 , wherein b is greater than 0.5 and less than or equal to 0.95.
3. The inorganic reaction system according to claim 1 , wherein c is at least 0.05, and no more than 0.3.
4. The inorganic reaction system according to claim 1 , wherein d is at least about 0.002, and no more than 0.1.
5. The inorganic reaction system according to claim 1 , wherein g is at least 0.05, and no more than about 0.3.
6. The inorganic reaction system according to claim 1 , wherein b:c is between about 70:30 to about 95:5.
7. The inorganic reaction system according to claim 1 , wherein b:g is between about 60:40 to 90:10.
8. The inorganic reaction system according to claim 1 , wherein the lead-bismuth-tellurium-silicate composition is formed from at least about 0.05 wt % lead-containing compound, and no more than about 1 wt % lead-containing compound, based upon 100% total weight of the inorganic reaction system.
9. The inorganic reaction system according to claim 1 , wherein the lead-bismuth-tellurium-silicate composition is formed from at least about 30 wt % bismuth-containing compound, and no more than about 90 wt % bismuth-containing compound, based upon 100% total weight of the inorganic reaction system.
10. The inorganic reaction system according to claim 1 , wherein the lead-bismuth-tellurium-silicate composition is formed from at least about 2 wt % tellurium-containing compound, and no more than about 15 wt % tellurium-containing composition, based upon 100% total weight of the inorganic reaction system.
11. The inorganic reaction system according to claim 1 , wherein the lead-bismuth-tellurium-silicate composition is formed from at least about 5 wt % silicon-containing compound, and no more than about 55 wt % silicon-containing composition, based upon 100% total weight of the inorganic reaction system.
12. The electroconductive paste according to claim 1 , further comprising a contact-promoting inorganic reaction system.
13. The electroconductive paste according to claim 12 , wherein the contact-promoting inorganic reaction system is a lead-bismuth-tellurium inorganic reaction system.
14. The electroconductive paste composition according to claim 1 , wherein the electroconductive paste comprises at least about 1 wt % of the at least one inorganic reaction system, and no more than about 10 wt %, based upon 100% total weight of the paste.
15. An electroconductive paste comprising:
metallic particles;
at least one inorganic reaction system comprising a lead-bismuth-tellurium-silicate composition of Formula (I):
Pb a —Bi b —Te c —Si g -M d -O e ,
wherein 0<a≤0.01,
0.2<b≤0.95,
0≤c≤0.5,
0<d≤0.2,
0<g≤0.5, and
the sum of a, b, c, d and g is 1,
a:b is between about 0.1:99.9 to about 5:95,
b:c is between about 50:50 to 99:1,
a:c is between about 1:99 to about 10:90,
b:g is between about 50:50 to about 98:2, and
M is one or more elements selected from the group consisting of boron, aluminum, gallium, germanium, tin, phosphorus, antimony, niobium, tantalum, vanadium, titanium, molybdenum, tungsten, chromium, silver, halides, chalcogenides, alkaline metals, alkaline earth metals, and rare earth metals, and
e is a number sufficient to balance the charge of the Pb, Bi, Te, Si, and M components; and
an organic vehicle,
wherein the at least one inorganic reaction system is formed from no more than about 1 wt % lead-containing compound based on 100% total weight of the inorganic reaction system.