Portland cement-based composition with improved pigment dispersion and color consistency
A tintable cement-based composition that includes a cement-based powder component and a pigment component. The powder component includes Portland cement, a filler, calcium sulfate hemihydrate, aluminum oxide, and Sepiolite clay; and the pigment component includes at least one pigment. The components can be packaged separately and mixed with water at the point of use.
1. A cement-based composition comprising:
a cement-based powder component comprising Portland cement, filler, calcium sulfate hemihydrate, aluminum oxide, and Sepiolite clay; and
a pigment component comprising at least one pigment;
the cement-based composition exhibiting color tolerance values of DL=0+/−3.0, Da=0+/−1.5, and Db=0+/−1.5 when tested according to at least one of Water Content Test Method I and Water Soak Test Method I.
2. The cement-based composition of claim 1 , wherein the composition exhibits color tolerance values of DL=0+/−3.0, Da=0+/−1.5, and Db=0+/−1.5 when tested according to the Water Content Test Method I.
3. The cement-based composition of claim 1 , wherein the composition exhibits color tolerance values of DL=0+/−3.0, Da=0+/−1.5, and Db=0+/−1.5 when tested according to the Water Soak Test Method I.
4. The cement-based composition of claim 1 , wherein the cement-based powder component comprises from about 15% by weight to about 50% by weight Portland cement.
5. The cement-based composition of claim 1 , wherein the cement-based powder component comprises from about 30% by weight to about 70% by weight filler.
6. The cement-based composition of claim 1 , wherein the cement-based powder component comprises from about 0.1% by weight to about 10% by weight calcium sulfate hemi-hydrate.
7. The cement-based composition of claim 1 , wherein the cement-based powder component comprises from about 0.1% by weight to about 5% by weight aluminum oxide.
8. The cement-based composition of claim 1 , wherein the cement-based powder component comprises from about 0.05% by weight to about 3% by weight Sepiolite clay.
9. The cement-based composition of claim 1 , wherein the filler is selected from the group consisting of silica sand, calcium carbonate, and combination thereof.
10. The cement-based composition of claim 1 , wherein the pigment component comprises a mixture of at least two different pigments.
11. A tintable cement-based powder comprising:
Portland cement;
filler;
calcium sulfate hemi-hydrate;
aluminum oxide; and
Sepiolite clay.
12. The tintable cement-based powder of claim 11 , comprising:
from about 0.1% by weight to about 10% by weight calcium sulfate hemi-hydrate;
from about 0.1% by weight to about 5% by weight aluminum oxide; and
from 0.05% by weight to about 3% by weight Sepiolite clay.
13. The tintable cement-based powder of claim 11 , comprising:
from about 0.1% by weight to about 5% by weight calcium sulfate hemi-hydrate;
from about 0.1% by weight to about 3% by weight aluminum oxide; and
from 0.05% by weight to about 2% by weight Sepiolite clay.
14. The tintable cement-based powder of claim 11 , comprising:
from 0.5% by weight to about 2.5% by weight calcium sulfate hemi-hydrate;
from 0.3% by weight to about 2% by weight aluminum oxide; and
from 0.1% by weight to about 1% by weight Sepiolite clay.
15. The tintable cement-based powder of claim 11 , wherein the tintable cement-based powder exhibits color tolerance values of DL=0+/−3.0, Da=0+/−1.5, and Db=0+/−1.5 when tested according to at least one of Water Soak Test Method II, Water Content Test Method II, Water Absorption Test Method II and Water Droplet Test Method II.
16. The tintable cement-based powder of claim 11 , wherein the tintable cement-based powder exhibits color tolerance values of DL=0+/−3.0, Da=0+/−1.5, and Db=0+/−1.5 when tested according to Water Droplet Test Method II, Water Content Test Method II, and Water Soak Test Method H.
17. The tintable cement-based powder of claim 11 , wherein the tintable cement-based powder exhibits color tolerance values of DL=0+/−3.0, Da=0+/−1.5, and Db=0+/−1.5 when tested according to Water Content Test Method II and Water Soak Test Method II.
18. The tintable cement-based powder of claim 11 , wherein the filler is selected from the group consisting of silica sand, calcium carbonate, and combinations thereof.
19. A tinted cement-based composition comprising:
the tintable cement-based powder of claim 11 ; and
from 0.1% by weight to no greater than 10% by weight pigment.
20. A method for grouting a tile joint, the method comprising
combining the cement-based composition of claim 1 and water to produce a tinted grout paste;
applying the tinted grout paste to the joint; and
allowing the tinted grout to cure.
21. The method of claim 20 , wherein the combining comprises combing the tintable cement-based composition with from about 15% by weight to about 30% by weight water based on the weight of the powder.
22. A method for tinting and grouting a tile joint, the method comprising:
mixing the tintable cement-based powder of claim 11 with a pigment and water to produce a tinted grout paste;
applying the tinted grout paste to the joint; and
allowing the tinted grout to cure.
23. A kit for providing a tinted grout comprising:
the cement-based composition of claim 1 ; and
instructions for mixing the powder component, the pigment, and water to provide a tinted grout.
24. A kit for providing a tinted grout comprising:
the tintable cement-based powder of claim 11 ; and
instructions for mixing the tintable cement-based powder with at least one pigment and water to provide a tinted grout.
25. The cement-based composition of claim 1 , comprising:
from about 0.1% by weight to about 10% by weight calcium sulfate hemi-hydrate;
from about 0.1% by weight to about 5% by weight aluminum oxide; and
from 0.05% by weight to about 3% by weight Sepiolite clay.
26. The cement-based composition of claim 1 , comprising:
from about 0.1% by weight to about 5% by weight calcium sulfate hemi-hydrate;
from about 0.1% by weight to about 3% by weight aluminum oxide; and
from 0.05% by weight to about 2% by weight Sepiolite clay.
27. The cement-based composition of claim 1 , comprising:
from 0.5% by weight to about 2.5% by weight calcium sulfate hemi-hydrate;
from 0.3% by weight to about 2% by weight aluminum oxide; and
from 0.1% by weight to about 1% by weight Sepiolite clay.