Black ceramic additives, pigments, and formulations
Ceramic black materials for use as, or in, colorants, inks, pigments, dyes, additives and formulations utilizing these black materials. Black ceramics having silicon, oxygen and carbon, and methods of making these ceramics; formulations utilizing these black ceramics; and devices, structures and apparatus that have or utilize these formulations. Plastics, paints, inks, coatings, formulations, liquids and adhesives containing ceramic black materials, preferably polymer derived black ceramic materials, and in particular polysilocarb polymer derived ceramic materials. The instant materials are particles which are pyrolyzed and are defined by having a specific Si, C and O content and having carbon which is both free and silicon bound. The particles are prepared by specific processes, as defined herein.
1. A method for making a black ceramic pigment, the method comprising: placing a polymer derived ceramic precursor on a forming surface, curing the polymer derived ceramic precursor on the forming surface, removing the cured polymer derived ceramic precursor from the forming surface, pyrolizing the cured polymer derived ceramic precursor, and thereby forming a black polymer derived ceramic pigment comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; and, wherein 20 weight % to 80 weight % of the carbon is free carbon.
2. A method for making a black ceramic pigment, the method comprising: placing a polymer derived ceramic precursor on a forming surface, curing the polymer derived ceramic precursor on the forming surface, removing the cured polymer derived ceramic precursor from the forming surface, pyrolizing the cured polymer derived ceramic precursor, and thereby forming a black polymer derived ceramic pigment comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; and, wherein 20 weight % to 80 weight % of the carbon is silicon-bound-carbon.
3. A method for making a black ceramic pigment, the method comprising: placing a polymer derived ceramic precursor on a forming surface, curing the polymer derived ceramic precursor on the forming surface, removing the cured polymer derived ceramic precursor from the forming surface, pyrolizing the cured polymer derived ceramic precursor, and thereby forming a black polymer derived ceramic pigment comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; and, wherein the cured polymer derived ceramic is reduced in size by action of removal from the forming surface.
4. A method for making a black ceramic pigment aggregate, the method comprising: pyrolizing a polymer derived ceramic to form black polymer derived ceramic bulk material, reducing the size of the polymer derived ceramic bulk material to form primary pigment particles having a particle size D 50 of from about 3 μm to about 0.1 μm, the primary pigment particles comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % free carbon.
5. The method of claim 4 , wherein primary pigment particles have a particle size D 50 of from about 2 μm to about 0.1 μm.
6. The method of claim 4 , wherein primary pigment particles have a particle size D 50 of from about 1 μm to about 0.1 μm.
7. The method of claim 4 , wherein primary pigment particles have a particle size D 50 of from about 0.9 μm to about 0.1 μm.
8. The method of claim 4 , wherein the black polysilocarb derived ceramic pigment is hydrophilic.
9. The method of claim 4 , wherein the black polysilocarb derived ceramic pigment is rendered hydrophobic.
10. A method for making a black ceramic pigment aggregate, the method comprising: pyrolizing a polymer derived ceramic to form black polymer derived ceramic bulk material, reducing the size of the polymer derived ceramic bulk material to form primary pigment particles having a particle size D 50 of from about 3 μm to about 0.1 μm, the primary pigment particles comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % silicon-bound-carbon.
11. The method of claim 10 , wherein primary pigment particles have a particle size D 50 of from about 2 μm to about 0.1 μm.
12. The method of claim 10 , wherein primary pigment particles have a particle size D 50 of from about 1 μm to about 0.1 μm.
13. The method of claim 10 , wherein primary pigment particles have a particle size D 50 of from about 0.9 μm to about 0.1 μm.
14. The method of claim 10 , wherein the black polysilocarb derived ceramic pigment is hydrophilic.
15. A method for making a black ceramic pigment, the method comprising: placing a polymer derived ceramic precursor on a forming surface, curing the polymer derived ceramic precursor on the forming surface, removing the cured polymer derived ceramic precursor from the forming surface, pyrolizing the cured polymer derived ceramic precursor, and thereby forming a black polymer derived ceramic pigment comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; wherein the pyrolized polymer derived ceramic is reduced in size to form a primary pigment particle; wherein the primary pigment particle has a particle size D 50 of less than about 4 μm; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % free carbon.
16. A method for making a black ceramic pigment, the method comprising: placing a polymer derived ceramic precursor on a forming surface, curing the polymer derived ceramic precursor on the forming surface, removing the cured polymer derived ceramic precursor from the forming surface, pyrolizing the cured polymer derived ceramic precursor, and thereby forming a black polymer derived ceramic pigment comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; wherein the pyrolized polymer derived ceramic is reduced in size to form a primary pigment particle; wherein the primary pigment particle has a particle size D 50 of less than about 4 μm; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % silicon-bound-carbon.
17. A method for making a black ceramic pigment, the method comprising: placing a polymer derived ceramic precursor on a forming surface, curing the polymer derived ceramic precursor on the forming surface, removing the cured polymer derived ceramic precursor from the forming surface, pyrolizing the cured polymer derived ceramic precursor, and thereby forming a black polymer derived ceramic pigment comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; wherein the pyrolized polymer derived ceramic is reduced in size to form a primary pigment particle; wherein the primary pigment particle has a particle size D 50 of from about 3 μm to about 0.1 μm; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % free carbon.
18. A method for making a black ceramic pigment, the method comprising: placing a polymer derived ceramic precursor on a forming surface, curing the polymer derived ceramic precursor on the forming surface, removing the cured polymer derived ceramic precursor from the forming surface, pyrolizing the cured polymer derived ceramic precursor, and thereby forming a black polymer derived ceramic pigment comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; wherein the pyrolized polymer derived ceramic is reduced in size to form a primary pigment particle; wherein the primary pigment particle has a particle size D 50 of from about 3 μm to about 0.1 μm, and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % silicon-bound-carbon.
19. The method of claim 18 , wherein the black polysilocarb derived ceramic pigment is hydrophilic.
20. A method for making a black ceramic pigment aggregate, the method comprising: pyrolizing a polymer derived ceramic to form black polymer derived ceramic bulk material, reducing the size of the polymer derived ceramic bulk material to form primary pigment particles having a particle size D 50 of from about 3 μm to about 0.1 μm, the primary pigment particles comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; wherein the pigment defines a blackness selected from the group consisting of: PMS 433, Black 3, Black 3, Black 4, Black 5, Black 6, Black 7, Black 2 2×, Black 3 2×, Black 4 2×, Black 5 2×, Black 6 2×, and Black 7 2×; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % free carbon.
21. A method for making a black ceramic pigment aggregate, the method comprising: pyrolizing a polymer derived ceramic to form black polymer derived ceramic bulk material, reducing the size of the polymer derived ceramic bulk material to form primary pigment particles having a particle size D 50 of from about 3 μm to about 0.1 μm, the primary pigment particles comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; wherein the pigment defines a blackness selected from the group consisting of: PMS 433, Black 3, Black 3, Black 4, Black 5, Black 6, Black 7, Black 2 2×, Black 3 2×, Black 4 2×, Black 5 2×, Black 6 2×, and Black 7 2×; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % silicon-bound-carbon.
22. A method for making a black ceramic pigment aggregate, the method comprising: pyrolizing a polymer derived ceramic to form black polymer derived ceramic bulk material, reducing the size of the polymer derived ceramic bulk material to form primary pigment particles having a particle size D 50 of from about 3 μm to about 0.1 μm, the primary pigment particles comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; wherein the pigment defines a blackness selected from the group consisting of: Tri-stimulus Colorimeter of X from about 0.05 to about 3.0, Y from about 0.05 to about 3.0, and Z from about 0.05 to about 3.0; a CIE L a b of L of less than about 40; a CIE L a b of L of less about 20; a CIE L a b of L of less than 50, b of less than 1.0 and a of less than 2; and a jetness value of at least about 200 M y ; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % free carbon.
23. A method for making a black ceramic pigment aggregate, the method comprising: pyrolizing a polymer derived ceramic to form black polymer derived ceramic bulk material, reducing the size of the polymer derived ceramic bulk material to form primary pigment particles having a particle size D 50 of from about 3 μm to about 0.1 μm, the primary pigment particles comprising from about 30 weight % to about 60 weight % silicon, from about 5 weight % to about 40 weight % oxygen, and from about 3 weight % to about 35 weight % carbon; wherein the pigment defines a blackness selected from the group consisting of: Tri-stimulus Colorimeter of X from about 0.05 to about 3.0, Y from about 0.05 to about 3.0, and Z from about 0.05 to about 3.0; a CIE L a b of L of less than about 40; a CIE L a b of L of less about 20; a CIE L a b of L of less than 50, b of less than 1.0 and a of less than 2; and a jetness value of at least about 200 M y ; and, wherein the carbon in the primary pigment particles is 20 weight % to 80 weight % silicon-bound-carbon.