Superabsorbent polymers with improved odor control capacity and process for the production thereof
View Patent ↗The present invention relates to a water-absorbing polymer and to a process for preparation, including finishing the water-absorbing polymer, with 0.0001 to 3% by weight, of a peroxo compound, based on the acrylic acid, after the polymerization is treated, and to a process for producing a hydrogel polymer, to the product of the process and to use.
1. A process for preparing water-absorbing polymers, comprising the process steps of
(i) mixing
(α1) 0.1 to 99.999% by weight of polymerized, ethylenically unsaturated monomers bearing acid groups, or salts of polymerized, ethylenically unsaturated monomers bearing acid groups, or polymerized, ethylenically unsaturated monomers comprising a protonated nitrogen, polymerized, ethylenically unsaturated monomers comprising a quaternized nitrogen, or mixtures thereof;
(α2) 0 to 69.999% by weight of polymerizable, ethylenically unsaturated monomers copolymerizable with (α1),
(α3) 0.001 to 10% by weight of one or more crosslinkers,
(α4) 0 to 30% by weight of water-soluble polymers,
(α5) 0-90% by weight of water, and
(α6) 0-20% by weight of one or more additives where the sum of the weights of (α1) to (α6) is 100% by weight,
(ii) free-radical polymerization with crosslinking to form a water-insoluble, aqueous untreated hydrogel polymer,
(iii) comminuting the hydrogel polymer,
(iv) drying the hydrogel polymer,
(v) grinding and sieving the hydrogel polymer to size,
(vi) surface post-crosslinking the ground and sieved hydrogel polymer and
(vii) finishing the water-absorbing polymer,
wherein
the water-absorbing polymer has been treated with 0.0001 to 3% by weight of a peroxo compound based on (α1), after the polymerization; and the peroxo compound is selected from the group consisting of alkali metal or alkaline earth metal peroxomonosulphate, peroxodisulphate, sulpho monoperacid and peroxomonosulphate triple salt.
2. The process according to claim 1 , wherein the water-absorbing polymer has been treated with 0.0001 to 1.5% by weight of a peroxo compound based on (α1), after the polymerization.
3. The process according to claim 1 , characterized in that the peroxo compound is added in steps (iii), (iv), (v), (vi) and/or (vii).
4. The process according to claim 1 , wherein the peroxo compound is added in step (vii).
5. The process according to claim 1 , wherein (α1) is 0.1 to 99.999% by weight of polymerized, ethylenically unsaturated monomers bearing acid groups.
6. The process according to claim 1 , wherein the peroxomonosulfate triple salt is potassium peroxymonosulfate.