Non-alkali glass substrate

1. A non-alkali glass substrate, having a strain point of 685° C. or higher and 750° C. or lower, an average thermal expansion coefficient at 50 to 350° C. of from 35×10 −7 to 43×10 −7 /° C., a specific gravity of from 2.50 to 2.80, a photoelastic constant of 25 nm/MPa/cm or more and less than 29 nm/MPa/cm, and a temperature (T 4 ) at which viscosity reaches 10 4 dPa·s of 1,250° C. or higher and lower than 1,350° C., and comprising, indicated by mol % on the basis of oxides,

63% or more and 68% or less of SiO 2 ,

12.2% or more and 14% or less of Al 2 O 3 ,

0.5% or more and less than 3% of B 2 O 3 ,

6.5% or more and 13% or less of MgO,

0% or more and less than 4% of CaO,

0% or more and 9% or less of SrO, and

0% or more and 10% or less of BaO,

wherein

MgO+CaO+SrO+BaO is from 15 to 20%, and

SrO+BaO is from 4 to 10%.

2. The non-alkali glass substrate according to claim 1 , having a glass transition temperature of from 750 to 810° C.

3. The non-alkali glass substrate according to claim 1 , having a devitrification temperature of 1,200° C. or higher and lower than 1,370° C., and a temperature (T 2 ) at which the viscosity reaches 10 2 dPa·s of 1,600° C. or higher and lower than 1,710° C.

4. The non-alkali glass substrate according to claim 1 , having a Young's modulus of from 76 to 90 GPa.

5. A non-alkali glass substrate, having a strain point of 685° C. or higher and 750° C. or lower, an average thermal expansion coefficient at 50 to 350° C. of from 35×10 −7 to 43×10 −7 /° C., a specific gravity of from 2.50 to 2.80, a photoelastic constant of 25 nm/MPa/cm or more and less than 29 nm/MPa/cm, and a temperature (T 4 ) at which viscosity reaches 10 4 dPa·s of 1,250° C. or higher and 1,335° C. or lower, and comprising, indicated by mol % on the basis of oxides,

63% or more and 67% or less of SiO 2 ,

12.2% or more and 14% or less of Al 2 O 3 ,

3% or more and less than 4.3% of B 2 O 3 ,

7% or more and 13% or less of MgO,

0% or more and 9% or less of CaO,

0% or more and 3% or less of SrO, and

0% or more and 7% or less of BaO,

wherein

MgO+CaO+SrO+BaO is from 15 to 20%, and

with the proviso that the CaO, SrO, and BaO concentrations are within the above-recited ranges and are linked to the B 2 O 3 concentration according to the following expressions:

CaO is from (6×B 2 O 3 −21)% to (6×B 2 O 3 −14)%, and

SrO+BaO is from (−6×B 2 O 3 +19)% to (−6×B 2 O 3 +28)%.

6. The non-alkali glass substrate according to claim 5 , having a glass transition temperature of from 740 to 790° C.

7. The non-alkali glass substrate according to claim 5 , having a devitrification temperature of 1,200° C. or higher and lower than 1,350° C. and a temperature (T 2 ) at which the viscosity reaches 10 2 dPa·s of from 1,600° C. or higher and 1,730° C. or lower.

8. The non-alkali glass substrate according to claim 5 , having a Young's modulus of from 76 to 88 GPa.