Steel material and impact absorbing member
View Patent ↗The steel material for an impact absorbing member has a composition containing: by mass %, C: 0.05 to 0.18%, Mn: 1 to 3%, Si+Al: at least 0.5% and less than 2.5%, and N: 0.001 to 0.015%, and in some cases, Cr: at most 0.5%, Mo: at most 0.2%, Ti: at most 0.05%, Nb: at most 0.05%, V: at most 0.2%, and B: at most 0.002%, the remainder being Fe and impurities. The steel material structure contains at least 70% by area of bainite made up of a lath structure having an average interval of at most 1 mm and martensite, 5 to 30%, and satisfies Formulas (1) and (2): (1) 1.2 £ H M0 /H B0 £ 1.6, (2) 0.90 £ {(H M10 /H M0 )/(H B10 /H B0 ) £ 1.3, where H M0 and H M10 represent average nano hardness in an initial state and after 10% tensile deformation of the martensite, and H B0 and H B0 represent that of bainite, respectively.
1. A steel material, comprising:
a chemical composition containing: by mass %, C: at least 0.05% and at most 0.18%, Mn: at least 1% to at most 3%, Si+Al: at least 0.5% and less than 2.5%, and N: at least 0.001% and at most 0.015%, Cr: 0 to 0.5%, Mo: 0 to 0.2%, Ti: 0 to 0.05%, Nb: 0 to 0.05%, V: 0 to 0.2%, and B: 0 to 0.002%, the remainder being Fe and impurities; and
a steel structure containing: by area %, bainite made up of a lath structure having an average interval of at most 1 μm: at least 70%, and martensite: 5% to 30%, the steel structure satisfying the following Formulas (1) and (2):
1.2≦ H M0 /H B0 ≦1.6 (1)
0.90≦{( H M10 /H M0 )/( H B10 /H B0 )≦1.3 (2)
wherein
H M0 represents initial average nano hardness of the martensite,
H BO represents initial average nano hardness of the bainite,
H M10 represents average nano hardness of the martensite after 10% tensile deformation, and
H B10 represents average nano hardness of the bainite after 10% tensile deformation.
2. The steel material set forth in claim 1 , wherein
the chemical composition, by mass %, contains one or two selected from the group consisting of Cr: 0.1 to 0.5% and Mo: 0.1 to 0.2%.
3. The steel material set forth in claim 1 , wherein
the chemical composition, by mass %, contains one or more selected from the group consisting of Ti: 0.002 to 0.05%, Nb: 0.002 to 0.05%, and V: 0.002 to 0.2%.
4. The steel material set forth in claim 1 , wherein
the chemical composition contains, by mass %, B: 0.0001 to 0.002%.
5. The steel material set forth in claim 1 , wherein
at least one surface has a plated layer.
6. An impact absorbing member, comprising
an impact absorbing portion for absorbing impact energy by being axially crashed and buckled, wherein
the impact absorbing portion is made of the steel material set forth in claim 1 .
7. An impact absorbing member, comprising
an impact absorbing portion for absorbing impact energy by being crashed in bending and plastically deformed, wherein
the impact absorbing portion is made of the steel material set forth in claim 1 .