Emulsion coagulant
View Patent ↗An object of the present invention is to provide an emulsion coagulant which can be used to quickly coagulate a tire puncture sealing material in an extremely low temperature environment. The emulsion coagulant of the present invention is an emulsion coagulant comprising: component (A) having a particle size of from 35 to 100 μm and comprising at least one type selected from the group consisting of aluminum oxide, magnesium oxide, and silicon oxide; propylene glycol alginate; and component (B) comprising at least one type selected from the group consisting of calcium oxide, calcium chloride, calcium acetate, and urea; the amount of component (B) being from 3 to 30 mass % of the total amount of component (A), propylene glycol alginate, and component (B); and the emulsion coagulant being used to coagulate a tire puncture sealing material comprising an emulsion.
1. An emulsion coagulant comprising:
component (A) having a particle size of from 35 to 100 μm and comprising at least one type selected from the group consisting of aluminum oxide, magnesium oxide, and silicon oxide;
propylene glycol alginate; and
component (B) comprising at least one type selected from the group consisting of calcium oxide, calcium chloride, calcium acetate, and urea;
an amount of component (B) being from 3 to 30 mass % of a total amount of the component (A), the propylene glycol alginate, and the component (B); and
the emulsion coagulant being used to coagulate a tire puncture sealing material comprising an emulsion.
2. The emulsion coagulant according to claim 1 , wherein the emulsion is at least one selected from the group consisting of natural rubber latex and a synthetic resin emulsion, and the tire puncture sealing material further comprises an antifreezing material.
3. The emulsion coagulant according to claim 2 , wherein the antifreezing material comprises at least one type selected from the group consisting of ethylene glycol, propylene glycol, and diethylene glycol.
4. The emulsion coagulant according to claim 1 , wherein the amount of the emulsion coagulant that is used is at least 10 parts by mass per 100 parts by mass of the tire puncture sealing material.
5. The emulsion coagulant according to claim 1 , wherein the component (B) comprises at least one type selected from the group consisting of calcium oxide, calcium chloride, and calcium acetate, and the emulsion comprises at least natural rubber latex.
6. The emulsion coagulant according to claim 1 , wherein the emulsion coagulant is used in an environment with a temperature of from −40° C. to +70° C.
7. The emulsion coagulant according to claim 1 , an amount of the component (A) is from 1.5 to 7 mass % of the amount of the tire puncture sealing material.