High-capacity negative electrode active material and lithium secondary battery including the same
View Patent ↗Disclosed are a high-capacity negative electrode active material and a lithium secondary battery including the same. More particularly, the negative electrode active material includes 50 wt % or more of an alkali metavanadate based on the total weight of a negative electrode active material, wherein the alkali metavanadate has a crystalline phase or an amorphous phase, and a composition of formula AVO 3 .
1. A negative electrode active material comprising
alkali metavanadate, and
graphite,
wherein the alkali metavandate is present in an amount of 50 wt % or more and less than 90 wt % based on the total weight of a negative electrode active material and the graphite is present in an amount of 10 wt % or more and less than 50 wt % based on the total weight of the negative electrode active material, and
wherein the alkali metavanadate has a crystalline phase or an amorphous phase and a composition of Formula 1 below:
AVO 3 (1)
wherein A is at least one alkali metal element of Na and K.
2. The negative electrode active material according to claim 1 , wherein the amorphous alkali metavanadate is a compound or mixture of AVO 3 and P 2 O 5 .
3. The negative electrode active material according to claim 2 , wherein the P 2 O 5 is comprised in an amount of 1 to 30 parts by weight based on 100 parts by weight of AVO 3 .
4. The negative electrode active material according to claim 1 , wherein a charge voltage of the negative electrode active material progresses up to less than 1.5 V with respect to reduction potential of lithium ions based on a negative electrode.
5. The negative electrode active material according to claim 1 , wherein a reversible capacity of the negative electrode active material is 400 mAh/g or more.
6. The negative electrode active material according to claim 1 , wherein when a charge voltage of the negative electrode active material progresses up to less than 0.1 V with respect to reduction potential of lithium ions based on a negative electrode, a reversible capacity of the negative electrode active material is 400 mAh/g or more.
7. The negative electrode active material according to claim 1 , wherein when a discharge voltage of the negative electrode active material progresses up to 2.5 V or more with respect to reduction potential of lithium ions based on a negative electrode, a reversible capacity of the negative electrode active material is 400 mAh/g or more.
8. The negative electrode active material according to claim 1 , wherein a vanadium (V) element comprised in the negative electrode active material reversibly stores three lithium elements or more.
9. The negative electrode active material according to claim 1 , wherein an average particle size of the alkali metavanadate is 1 to 30 μm.
10. The negative electrode active material according to claim 1 , wherein when X-ray diffraction of the amorphous phase is measured from 10 degrees to 80 degrees at a scan rate of 1 degree/minute to 16 degrees/minute and an interval of 0.01 degrees, a ratio of signal to noise is less than 50, compared to a noise shown in a base line.
11. A lithium secondary battery comprising:
a negative electrode comprising the negative electrode active material according to claim 1 ;
a positive electrode comprising at least one of a lithium metal oxide or lithium metal phosphate;
a separator disposed between the negative electrode and the positive electrode; and
an electrolyte.
12. The lithium secondary battery according to claim 11 , wherein the negative electrode operates in a voltage section of 0 V to 3.5 V with respect to lithium.
13. The lithium secondary battery according to claim 11 , wherein, in the positive electrode, the lithium metal oxide is LiMO 2 , where M is Co, Ni, or Mn, Li 1+x Mn 2−x O 4 , where 0≤x≤0.3, or LiNi 1−x M x O 2 , where M is Co, Mn, Al, Cu, Fe, Mg, B or Ga, and 0.01≤x≤0.3, and the lithium metal phosphate is LiMPO 4 , where M is Fe, Co, Ni, or Mn.
14. The lithium secondary battery according to claim 11 , wherein, in the positive electrode, the lithium metal oxide is LiCoO 2 , LiNiO 2 , LiMn 2 O 4 , Li(Ni a Mn b Co c )O 2 , where a+b+c=1, LiNi 0.5 Mn 0.5 O 4 , or LiNi 0.5 Mn 0.5 O 2 , and the lithium metal phosphate is LiFePO 4 , LiMnPO 4 , or Li 3 V 2 (PO 4 ) 3 .
15. The lithium secondary battery according to claim 11 , wherein the lithium metal oxide and lithium metal phosphate of the positive electrode are at least one of LiNi 0.5 Mn 1.5 O 4 , LiCoPO 4 , Li 3 V 2 (PO 4 ) 3 and yLi 2 MnO 3 .(1-y)LiNi a Mn b Co c O 2 , where 0.2≤y≤0.8 and a+b+c=1, operable at a voltage of 4.5 V or more.
16. The lithium secondary battery according to claim 11 , wherein the electrolyte comprises an organic solvent and a lithium salt, the organic solvent comprises at least one of ethylene carbonate, propylene carbonate, diethyl carbonate, dimethyl carbonate, 1,2-dimethoxyethane, 1,2-diethoxyethane, γ-butyrolactone, tetrahydrofuran, 2-methyltetrahydrofuran, 1,3-dioxene, 4-methyl-1,3-dioxene, diethyl ether, and sulfolane, and the lithium salt comprises at least one of LiClO 4 , LiCF 3 SO 3 , LiAsF 6 , LiBF 4 , LiN(CF 3 SO 2 ) 2 , LiPF 6 , LiSCN, LiB(C 2 O 4 ) 2 , and LiN(SO 2 C 2 F 5 ) 2 .
17. A method of manufacturing an electrode, the method comprising:
mixing a binder and a dispersion with a powder of the negative electrode active material according to claim 1 to prepare a paste;
spreading the paste over a current collector for an electrode; and
drying the paste at 50 to 200° C.
18. The method according to claim 17 , wherein, in the preparing of the paste, a conductive material is additionally added and mixed, and the conductive material is at least one of powder type carbon black, vapor grown carbon fiber, and graphite, and is comprised in an amount of 1 to 30 parts by weight with respect to 100 parts by weight of the negative electrode active material.
19. The method according to claim 17 , wherein, in the preparing of the paste, alkali metavanadate is an AVO 3 type, where A is at least one of Li, Na, and K, and is crystalline or amorphous.
20. The method according to claim 17 , wherein the dispersion is at least one of N-methylpyrrolidone (NMP), isopropyl alcohol, acetone and water, and is comprised in an amount of 10 to 200 parts by weight with respect to 100 parts by weight of the negative electrode active material; and the binder is at least one of polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVdF), cellulose, styrene butadiene rubber (SBR), polyimides, polyacrylic acid, alkali polyacrylate, polymethyl methacrylate (PMMA), and polyacrylonitrile (PAN), and is comprised in an amount of 3 to 50 parts by weight with respect to 100 parts by weight of the negative electrode active material.
21. The method according to claim 17 , wherein the current collector for the electrode is at least one of copper, aluminum, stainless, nickel, and titanium.
22. A negative electrode active material comprising
alkali metavanadate, and
graphite,
wherein the alkali metavandate is present in an amount of 50 wt % or more and less than 90 wt % based on the total weight of a negative electrode active material, and the graphite is present in an amount of 10 wt % or more and less than 50 wt % based on the total weight of the negative electrode active material,
wherein the alkali metavanadate has a crystalline phase and a composition of Formula 1 below:
AVO 3 (1)
wherein A is at least one alkali metal element of Na and K, and wherein the crystalline phase is irreversibly converted into an amorphous phase during charging.