Method for manufacturing high manganese hot-dip galvanized steel sheet with excellent coatability and ultra-high strength, and high manganese hot-dip galvanized steel sheet manufactured by said method
There are provided a method for manufacturing a high manganese hot-dip galvanized steel sheet having superior coatability and ultra-high strength, and a high manganese hot-dip galvanized steel sheet manufactured by the method. The method includes: cold rolling a hot-rolled steel sheet to form a cold-rolled steel sheet, the hot-rolled steel sheet including, by wt %, C: 0.3% to 1%, Mn: 8% to 25%, Si: 0.1% to 3%, Al: 0.01% to 8%, Cr: 0.1% to 2%, Ti: 0.01% to 0.2%, B: 0.0005% to 0.01%, Ni: 0.01% to 2%, Sn: 0.06% to 0.2%, and a balance of Fe and inevitable impurities; heating the cold-rolled steel sheet; cooling the heated steel sheet to, or maintaining the heated steel sheet; and performing a hot-dip galvanizing process on the cooled or temperature-maintained steel sheet by dipping the cooled or temperature-maintained steel sheet into a hot-dip galvanizing bath.
1. A high manganese hot-dip galvanized steel sheet comprising, by wt %, carbon (C): 0.3% to 1%, manganese (Mn): 8% to 25%, silicon (Si): 0.1% to 3%, aluminum (Al): 0.01% to 8%, chromium (Cr): 0.1% to 2%, titanium (Ti): 0.01% to 0.2%, boron (B): 0.0005% to 0.01%, nickel (Ni): 0.01% to 2%, tin (Sn): 0.06% to 0.2%, and a balance of iron (Fe) and inevitable impurities,
wherein discontinuous particle-shaped Si oxides of a thickness of 5 μm to 10 μm are formed on the steel sheet before the steel sheet is hot-dip galvanized, and non-galvanized regions of the high manganese hot-dip galvanized steel sheet have an average diameter of 1 mm or less, including 0 mm, and
wherein the high manganese hot-dip galvanized steel sheet has a tensile strength of 1200 MPa or greater and an elongation of 7% or greater.
2. The high manganese hot-dip galvanized steel sheet of claim 1 , wherein the non-galvanized regions have an average diameter of 0.5 mm or less.
3. The high manganese hot-dip galvanized steel sheet of claim 1 , wherein the non-galvanized regions have an average diameter of 0.3 mm or less.
4. A high manganese hot-dip galvanized steel sheet manufactured by a method comprising cold rolling a hot-rolled steel sheet at a reduction ratio of 30% to 60% to form a cold-rolled steel sheet; heating the cold-rolled steel sheet under conditions of a dew point temperature ranging from −30° C. to −80° C. and a heating temperature ranging from 450° C. to 650° C.; cooling the heated steel sheet to, or maintaining the heated steel sheet at, a temperature within a range of 450° C. to 500° C.; and performing a hot-dip galvanizing process on the cooled or temperature-maintained steel sheet by dipping the cooled or temperature-maintained steel sheet into a hot-dip galvanizing bath containing aluminum (Al) in an amount of 0.13 wt % to 0.25 wt % and maintained at a temperature of 450° C. to 500° C., wherein the high manganese hot-dip galvanized steel sheet comprises, by wt %,
carbon (C): 0.3% to 1%,
manganese (Mn): 8% to 25%,
silicon (Si): 0.1% to 3%,
aluminum (Al): 0.01% to 8%,
chromium (Cr): 0.1% to 2%,
titanium (Ti): 0.01% to 0.2%,
boron (B): 0.0005% to 0.01%,
nickel (Ni): 0.01% to 2%,
tin (Sn): 0.06% to 0.2%, and
a balance of iron (Fe) and inevitable impurities,
wherein discontinuous particle-shaped Si oxides of a thickness of 5 μm to 10 μm are formed on the steel sheet before the steel sheet is hot-dip galvanized, and non-galvanized regions of the high manganese hot-dip galvanized steel sheet have an average diameter of 1 mm or less, including 0 mm, and
wherein the high manganese hot-dip galvanized steel sheet has a tensile strength of 1200 MPa or greater and an elongation of 7% or greater.