Method for preparing continuous carbon fiber-reinforced thermoplastic prepreg
View Patent ↗The present invention relates to a method for preparing a continuous carbon fiber-reinforced thermoplastic prepreg, and more specifically, to a method for preparing a continuous carbon fiber-reinforced thermoplastic semi-prepreg or prepreg, comprising the steps of: providing a plurality of carbon fibers having an increased width; preparing a layered product by arranging a thermoplastic film on at least a part of the upper and lower portions of the carbon fibers having an increased width; and preparing a joined product by joining the thermoplastic film and the carbon fibers comprising the layered body.
1. A method for preparing a continuous carbon fiber reinforced thermoplastic prepreg, the method comprising:
preparing widely spread filaments of carbon fiber;
forming a stack by disposing a thermoplastic film on at least one side of upper and lower sides of the widely spread filaments of carbon fiber; and
forming a bonded material by bonding the thermoplastic film and the carbon fiber of the stack by radiating microwaves,
wherein the preparing of the widely spread filaments of carbon fiber comprises coating the filaments of carbon fiber with a bonding resin having a melting point lower than that of the thermoplastic film.
2. The method of claim 1 , wherein the widely spread filaments of carbon fiber are arranged at regular intervals.
3. The method of claim 1 , wherein the thermoplastic film is formed of a material selected from the group consisting of polypropylene (PP), polyamide (PA), polyetheretherketone (PEEK), and polyethyleneterephthalate (PET).
4. The method of claim 1 , wherein the thermoplastic film has a thickness of 10 μm to 100 μm.
5. The method of claim 1 , further comprising pressing the bonded material by using a pair of rollers under a vacuum or atmospheric pressure conditions.
6. The method of claim 5 , after the pressing is performed, further comprising:
heating the bonded material; and
additionally pressing the bonded material by using a pair of rollers under a vacuum or atmospheric pressure conditions.
7. The method of claim 6 , wherein the heating of the bonded material is performed using at least one heat source selected from the group consisting of halogen lamps and infrared lamps.
8. The method of claim 1 , wherein forming a stack is performed by disposing a thermoplastic film on both upper and lower sides of the widely spread filaments of carbon fiber.