Mixed coating material
A mixed coating material is obtained by mixing a cold curing resin that undergoes reaction curing at normal room temperature, and a fluororesin. The constituent ratio of the fluororesin in a coating film ranges from 43 wt % to 68 wt %.
1. A mixed coating material, consisting of:
a cold curing resin that undergoes reaction curing at normal room temperature; and
a tetrafluoroethylene resin including particulate bodies and having an average molecular weight ranging from 500 to 5000,
wherein a constituent ratio of the tetrafluoroethylene resin in a coating film that is a cured state of the mixed coating material ranges from 55 wt % to 67.3 wt %, and
wherein the cold curing resin is a polyurethane resin.
2. The mixed coating material according to claim 1 , wherein the water contact angle is from 140° or larger to 160° or smaller and the water sliding angle is from 2° or larger to 7° or smaller.
3. A mixed coating material, comprising:
a cold curing resin that undergoes reaction curing at normal room temperature; and
a tetrafluoroethylene resin having particulate bodies and having an average molecular weight ranging from 500 to 5000, wherein
a constituent ratio of the tetrafluoroethylene resin in a coating film that is a cured state of the mixed coating material ranges from 55 wt % to 67.3 wt %,
the cold curing resin is a polyurethane resin, and
a water contact angle in the cured state of the mixed coating material is 120° or larger and a water sliding angle is 10° or smaller, the water contact angle and the water sliding angle being measured at room temperature using a contact angle meter.
4. The mixed coating material according to claim 3 , wherein the water contact angle is from 140° or larger to 160° or smaller and the water sliding angle is from 2° or larger to 7° or smaller.