Embossed microporous membrane battery separator materials and methods of manufacture and use thereof
Disclosed are embossed microporous membranes, as well as articles (e.g., battery separators, materials, textiles, composites, and laminates) comprising the embossed microporous membranes. Also provided are methods of making and/or using embossed microporous membranes.
1. An embossed microporous membrane within a battery separator, where the embossed microporous membrane is prepared by a process comprising embossing, calendering or compressing a microporous polymer film made by a dry-stretch process and including a plurality of pores having a substantially round shape,
wherein the microporous polymer film exhibits a ratio of machine direction (MD) tensile strength to transverse direction (TD) tensile strength of from 0.5 to 5.0; and
wherein the microporous polymer film is a triple-ply film having a PP/PE/PP configuration; and
wherein the embossing pattern comprises embossed horizontal lines running parallel to the TD of the membrane;
wherein the horizontal lines have a line width of from 2 microns to 10 microns.
2. The membrane of claim 1 , wherein the embossed microporous membrane exhibits increased MD tensile strength, increased TD tensile strength, increased puncture strength, decreased MD splitting, or a combination thereof as compared to the microporous polymer film.
3. The membrane of claim 1 , wherein the horizontal lines have a spacing in the MD of from one to ten times the line width.
4. The membrane of claim 1 , wherein at least one of the PP layers comprises impact copolymer polypropylene.
5. The membrane of claim 1 , wherein the plurality of pores has an average pore size of from 0.03 microns to 0.50 microns and an aspect ratio of from 0.75 to 1.25; and
wherein the microporous polymer film has a porosity of from 20% to 80% and a TD tensile strength of at least 175 kg/cm 2 .
6. The membrane of claim 1 , wherein the microporous polymer film has at least one of a porosity of from 65% to 90%, a JIS Gurley of less than 60 seconds, a mean flow pore diameter of at least 0.05 microns, an Aquapore size of at least 0.08 microns, a TD tensile strength of at least 225 kg/cm 2 , a thickness of from 8 microns to 80 microns, a TD shrinkage of less than 6.0% at 90° C. and a TD shrinkage of less than 15.0% at 120° C.
7. The membrane of claim 1 , further comprising a nonwoven disposed on at least one side of the embossed microporous membrane.
8. An embossed microporous membrane within a battery separator, where the embossed microporous membrane comprises an embossed microporous polymer film, wherein the embossed microporous polymer film is a dry-stretch process film, has a thickness of from 2 microns to 20 microns, a porosity of from 20% to 65%, a JIS Gurley of 500 or less, and a ratio of MD tensile strength to TD tensile strength of from 0.5 to 5.0 wherein the microporous membrane is a triple-ply film having a PP/PE/PP configuration; and
wherein the embossing pattern comprises embossed horizontal lines running parallel to the TD of the membrane;
wherein the horizontal lines have a line width of from 2 microns to 10 microns.
9. The membrane of claim 8 , wherein the embossed microporous polymer film has at least one of a thickness of from 3 microns to 12 microns, a porosity of from 25% to 50%, a JIS Gurley of from 80 seconds to 500 seconds, a TD shrinkage of less than 6.0% at 90° C. and less than 15.0% at 120° C., a puncture strength of from 200 g to 325 g, a TD tensile strength of at least 250 kg/cm 2 , and an MD tensile strength of from 1000 kg/cm 2 to 2000 kg/cm 2 .
10. The membrane of claim 8 , further comprising a nonwoven disposed on a side of the embossed microporous polymer film.
11. A battery comprising an anode, a cathode, and the battery separator of claim 1 disposed between the anode and the cathode.