INTERMEDIATE COATING COMPOSITION, MULTILAYERED COATING FILM, AND METHOD FOR FORMING THE MULTILAYERED COATING FILM
An intermediate coating composition used in forming an intermediate coating layer directly overlaid on the surface of an electrodeposition coating layer constructing a vehicle outer panel, wherein a coating film obtained by curing of the intermediate coating composition alone has following characteristics (1) to (4): (1) a loss tangent (tan δ) at −20° C. as determined from a measurement of a dynamic viscoelasticity under a condition involving a rate of temperature rise of 2° C./min and a frequency of 8 Hz being 0.01 to 0.5; (2) a dynamic glass transition temperature being −15° C. to 55° C.; (3) percentage of elongation at −20° C. being 1% to 250%; and (4) a Young's modulus at −20° C. being 400 kgf/cm 2 to 50,000 kgf/cm 2 . The coating film obtained from the intermediate coating composition preferably further has the following characteristic (5): a tensile strength at −20° C. being 200 kgf/cm 2 to 1,200 kgf/cm 2 .
1 . An intermediate coating composition used in forming an intermediate coating layer directly overlaid on a surface of an electrodeposition coating layer constructing a vehicle outer panel, wherein
a coating film obtained by curing of the intermediate coating composition alone has following characteristics (1) to (4):
(1) a loss tangent (tan δ) at −20° C. as determined from a measurement of a dynamic viscoelasticity under a condition involving a rate of temperature rise of 2° C./min and a frequency of 8 Hz being no less than 0.01 and no greater than 0.5;
(2) a dynamic glass transition temperature (dynamic Tg) being no less than −15° C. and no greater than 55° C.;
(3) percentage of elongation at −20° C. being no less than 1% and no greater than 250%; and
(4) a Young's modulus at −20° C. being no less than 400 kgf/cm 2 and no greater than 50,000 kgf/cm 2 .
2 . The intermediate coating composition according to claim 1 , wherein the coating film has following characteristic (5):
(5) a tensile strength at −20° C. being no less than 200 kgf/cm 2 and no greater than 1,200 kgf/cm 2 .
3 . The intermediate coating composition according to claim 1 comprising a polycaprolactonetriol and a blocked isocyanate as resin components.
4 . The intermediate coating composition according to claim 1 comprising a laminar filler as a pigment component.
5 . A multilayered coating film comprising:
an electrodeposition coating layer constructing a vehicle outer panel; an intermediate coating layer directly overlaid on a surface of the electrodeposition coating layer; and
a top coating layer overlaid on a surface of the intermediate coating layer,
wherein the intermediate coating layer is formed from the intermediate coating composition according to claim 1 .
6 . A multilayered coating film-forming method comprising:
forming an electrodeposition coating layer constructing a vehicle outer panel;
directly forming an intermediate coating layer overlaid on a surface of the electrodeposition coating layer; and
forming a top coating layer overlaid on a surface of the intermediate coating layer,
wherein the intermediate coating composition according to claim 1 is applied in forming the intermediate coating layer.