1. An ultraviolet curable resin composition for a self-lubricating liner, the composition comprising:

a first (meth)acrylate compound having an isocyanuric acid ring represented by the following formula (1):

(wherein X is a group which contains an acryloyl group and is composed only of C, H, and O, and Y and Z are groups each composed only of C, H, and O);

a second (meth)acrylate compound different from the first (meth)acrylate compound;

a first polytetrafluoroethylene resin with an average particle size in the range of 75 μm to 180 μm; and

a second polytetrafluoroethylene resin with an average particle size in the range of 1 μm to 15 μm,

wherein a total amount of the first polytetrafluoroethylene resin and the second polytetrafluoroethylene resin is in the range of 30% by weight to 50% by weight with respect to an entire amount of the ultraviolet curable resin composition; and

the second polytetrafluoroethylene resin is contained in an amount of 20% by weight to 75% by weight with respect to the total amount of the first and second polytetrafluoroethylene resins.

2. The ultraviolet curable resin composition according to claim 1 , wherein the first (meth)acrylate compound is contained in an amount of 15% by weight to 35% by weight with respect to the entire amount of the ultraviolet curable resin composition; and

a total amount of the first (meth)acrylate compound and the second (meth)acrylate compound is in the range of 35% by weight to 65% by weight with respect to the entire amount of the ultraviolet curable resin composition.

3. The ultraviolet curable resin composition according to claim 1 , wherein a melting point of the first polytetrafluoroethylene resin is higher than a melting point of the second polytetrafluoroethylene resin.

4. The ultraviolet curable resin composition according to claim 1 , wherein the first (meth)acrylate compound having the isocyanuric acid ring represented by the formula (1) is one of di-(2-acryloxyethyl)isocyanurate, tris-(2-acryloxyethyl)isocyanurate, and ε-caprolactone modified tris-(2-acryloxyethyl)isocyanurate, or a mixture of the di-(2-acryloxyethyl)isocyanurate and the tris-(2-acryloxyethyl)isocyanurate.

5. The ultraviolet curable resin composition according to claim 1 , wherein the second (meth)acrylate compound includes at least one meth(acrylate) compound selected from the group consisting of: hydroxyethyl(meth)acrylate, hydroxypropyl (meth)acrylate and isobornyl (meth)acrylate; and

the at least one meth(acrylate) compound is contained in an amount of 5% by weight to 20% by weight with respect to the entire amount of the ultraviolet curable resin composition.

6. The ultraviolet curable resin composition according to claim 1 , wherein the second (meth)acrylate compound includes at least one meth(acrylate) compound selected from the group consisting of: pentaerythritol triacrylate, pentaerythritol tetraacrylate, dipentaerythritol penta(meth)acrylate, dipentaerythritol hexa(meth)acrylate, and dipentaerythritol polyacrylate; and

the at least one meth(acrylate) compound is contained in an amount of 8% by weight or less with respect to the entire amount of the ultraviolet curable resin composition.

7. The ultraviolet curable resin composition according to claim 1 , wherein the second (meth)acrylate compound includes bisphenol A-type epoxy modified acrylate; and the bisphenol A-type epoxy modified acrylate is contained in an amount of 10% by weight or less with respect to the entire amount of the ultraviolet curable resin composition.

8. The ultraviolet curable resin composition according to claim 1 , wherein the second (meth)acrylate compound includes at least one meth(acrylate) compound selected from the group consisting of: urethane acrylate, ethylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, butylene glycol di(meth)acrylate, hexanediol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, and tripropylene glycol di(meth)acrylate; and

the at least one meth(acrylate) compound is contained in an amount of 2% by weight or less with respect to the entire amount of the ultraviolet curable resin composition.

9. The ultraviolet curable resin composition according to claim 1 , wherein the first (meth)acrylate compound is a mixture of di-(2-acryloxyethyl)isocyanurate and tris-(2-acryloxyethyl)isocyanurate; and

the second (meth)acrylate compound is a mixture of bisphenol A-type epoxy modified acrylate, dipentaerythritol hexa(meth)acrylate, isobornyl (meth)acrylate, hydroxyethyl (meth)acrylate, and ethylene glycol di(meth)acrylate.

10. The ultraviolet curable resin composition according to claim 1 , further comprising a thermosetting agent.

11. A sliding member comprising a self-lubricating liner which is formed on a sliding surface of the sliding member and is made of the ultraviolet curable resin composition according to claim 1 .

12. The sliding member according to claim 11 , wherein the sliding member is a sliding bearing.

13. The sliding member according to claim 12 , wherein the sliding bearing is a spherical bearing.

14. The sliding member according to claim 11 , wherein the sliding member is a bolt comprising a head portion, a shaft portion, a thread portion, and the self-lubricating liner formed on an outer circumferential surface of the shaft portion.

15. A manufacturing method for producing a sliding member, comprising:

applying an ultraviolet curable resin composition on a sliding surface of the sliding member; and

curing the ultraviolet curable resin composition by irradiation with ultraviolet rays to form a self-lubricating liner,

wherein the ultraviolet curable resin composition comprises:

a first (meth)acrylate compound having an isocyanuric acid ring represented by the following formula (1):

(wherein X is a group which contains an acryloyl group and is composed only of C, H, and O and Y and Z are groups each composed only of C, H, and O);

a second (meth)acrylate compound different from the first (meth)acrylate compound;

a first polytetrafluoroethylene resin with an average particle size in the range of 75 μm to 180 μm; and

a second polytetrafluoroethylene resin with an average particle size in the range of 1 μm to 15 μm,

wherein a total amount of the first polytetrafluoroethylene resin and the second polytetrafluoroethylene resin is in the range of 30% by weight to 50% by weight with respect to an entire amount of the ultraviolet curable resin composition; and

the second polytetrafluoroethylene resin is contained in an amount of 20% by weight to 75% by weight with respect to the total amount of the first and second polytetrafluoroethylene resins.

16. The manufacturing method for producing the sliding member according to claim 15 , wherein the first (meth)acrylate compound is contained in an amount of 15% by weight to 35% by weight with respect to the entire amount of the ultraviolet curable resin composition; and

a total amount of the first (meth)acrylate compound and the second (meth)acrylate compound is in the range of 35% by weight to 65% by weight with respect to the entire amount of the ultraviolet curable resin composition.

17. The manufacturing method for producing the sliding member according to claim 15 , further comprising performing cutting or grinding of the self-lubricating liner to have a desired size.

18. The manufacturing method for producing the sliding member according to claim 15 ,

wherein the ultraviolet curable resin composition contains a thermosetting agent;

the sliding member is a spherical bearing including an outer race member which has a concave first bearing surface and an inner race member which has a convex second bearing surface slidably movable on the first bearing surface; and

the self-lubricating liner is formed by:

applying the ultraviolet curable resin composition on the concave first bearing surface or the convex second bearing surface as a sliding surface;

curing the ultraviolet curable resin composition applied on the concave first bearing surface or the convex second bearing surface until a semi-cured state by irradiation with the ultraviolet rays;

inserting the inner race member into the outer race member after the ultraviolet curable resin composition is semi-cured;

pressing the outer race member to cause plastic deformation so as to make the outer race member follow the convex second bearing surface of the inner race member; and

curing the ultraviolet curable resin composition completely by heat after the plastic deformation.