View Patent ↗An abrasion resistant flooring covering formed from a UV curable coating composition having binder and diamond particles—the abrasion resistant flooring covering used to overcoat the surface of flooring products or various abrasion heavy surfaces to protect such a products or surfaces from damage by abrasion or scratch.
1. A floor covering comprising
a substrate, and
a coating layer comprising:
a coating matrix formed from a curable coating composition comprising a binder, wherein the coating matrix has an average coating matrix thickness; and
diamond particles that have an average particle size and a narrow distribution of particle sizes, wherein the average article size is about 2 μm to about 50 μm and the narrow distribution of particle sizes has a standard deviation less than 35% of the average particle size;
wherein a ratio of the average coating matrix thickness to average particle size ranges from 0.6:1 to 2:1.
2. The floor covering of claim 1 wherein the coating layer comprises less than 5.5 wt. % of diamond particles based on the weight of the coating layer.
3. The floor covering of claim 2 wherein the coating layer comprises at least 1.5 wt. % of diamond particles based on the weight of the coating layer.
4. The floor covering of claim 1 wherein the average coating matrix thickness ranges from about 4 μm to about 40 μm.
5. The floor covering of claim 4 wherein the average coating matrix thickness ranges from about 6 μm to about 20 μm.
6. The floor covering of claim 1 wherein the average coating matrix thickness is about 6 μm.
7. The floor covering of claim 1 wherein the average coating matrix thickness is about 18 μm.
8. The floor covering of claim 1 wherein the average coating matrix thickness is measured from a top surface of the coating matrix to a bottom surface of the coating matrix and the diamond particles protrude from the top surface of the coating matrix at a distance ranging from about 1% to about 50% of the coating matrix thickness.
9. The floor covering of claim 1 wherein the average coating matrix thickness is measured from a top surface of the coating matrix to a bottom surface of the coating matrix and the diamond particles are submerged beneath the top surface of the coating matrix at a distance that is about 1% to about 50% of the coating matrix thickness.
10. The floor covering of claim 1 wherein the average coating matrix thickness is measured from a top surface of the coating matrix to a bottom surface of the coating matrix and the diamond particles are submerged beneath the top surface of the coating matrix at a first distance that is about 1% to about 25% of the coating matrix thickness and the diamond particles are vertically offset from the bottom surface of the coating matrix by a second distance that is about 1% to about 25% of the coating matrix thickness.
11. A floor covering comprising
a substrate, and
a coating layer comprising:
a coating matrix formed from a curable coating composition comprising a binder, and
diamond particles that have an average particle size ranging from about 2 μm to about 50 μm;
wherein the diamond particles have an average distance between two adjacently placed particles of from 20 μm to 75 μm.
12. The floor covering of claim 11 wherein the coating layer comprises about 1.5 wt. % to about 5.5 wt. % of the diamond particles based on the weight of the coating layer.
13. The floor covering of claim 11 wherein the coating matrix has an average coating matrix thickness and a ratio of the average coating matrix thickness to the average particle size ranges from 0.6:1 to 2:1.
14. The floor covering of claim 11 wherein the average coating matrix thickness ranges from 4 μm to 40 μm.
15. The floor covering of claim 14 wherein the average coating matrix thickness ranges from 6 μm to 20 μm.
16. The floor covering of claim 11 wherein the average coating matrix thickness is about 6 μm.
17. The floor covering of claim 11 wherein the average coating matrix thickness is about 18 μm.
18. A floor covering comprising
a substrate, and
a coating layer formed from a curable coating composition comprising:
a binder, and
abrasion resistant particles consisting essentially of diamond particles that have an average particle size and a narrow distribution of particle sizes, the narrow distribution of particle sizes has a standard deviation less than 35% of the average particle size;
wherein the diamond particles are present in an amount ranging from about 2 wt. % to about 5.5 wt. % based on the total weight of the coating layer.
19. The floor covering of claim 18 wherein the coating matrix has an average coating thickness ranging from about 4 μm to about 40 μm.
20. The floor covering of claim 18 wherein the coating matrix has an average coating thickness between 6 μm and 20 μm.