Zoned catalyst composites
Provided herein are zoned catalysts that utilize components efficiently in that relatively short zones are provided to achieve specific functionalities to convert and/or trap one or more components in the exhaust stream. Highly controlled zoned are formed from one end of a monolithic carrier. The zones have a flat profile such that the zoned catalytic material within each passage of the substrate is at a substantially uniform distance from one end of the carrier. Methods of making and using the same are also provided.
1. A zoned catalyst composite for an exhaust stream of an internal combustion engine comprising:
a monolithic carrier comprising a plurality of longitudinal passages;
a zone that begins from one end of the carrier and extends axially along the longitudinal passages such that the zone has a flat profile, the zone comprising a catalytic material that is effective to convert and/or trap one or more components in the exhaust stream;
wherein at least one of the following conditions is met: (i) the distance of the zone from the one end of the carrier varies in the range of 0 to 15% from passage-to-passage; and (ii) for each passage, the thickness of the zone at the one end of the carrier as compared to the thickness at the end of the zone varies in an amount of not more than 15%.
2. The zoned catalyst composite of claim 1 , wherein the component is carbon monoxide (CO), hydrocarbons (HC), nitrogen oxides (NOx), soot, ammonia (NH 3 ), SO x (SO 2 , SO 3 ) and/or hydrogen disulfide (H 2 S).
3. The zoned catalyst composite of claim 1 , wherein the zone comprises up to one inch (2.54 cm) of the carrier's length.
4. The zoned catalyst composite of claim 1 , wherein the zone comprises in the range of 2 mm to 0.5 inches (1.27 cm) carrier's length.
5. The zoned catalyst composite of claim 1 , wherein the catalytic material comprises a platinum group metal (PGM), a base metal (BM), an oxygen storage component (OSC), and/or a molecular sieve.
6. The zoned catalyst composite of claim 1 , wherein the zone has an average thickness in the range of 10-60 μm.
7. The zoned catalyst composite of claim 1 , wherein the zone is formed from a washcoat that is shear thinning having a pseudoplastic index in the range of 5-7.
8. The zoned catalyst composite of claim 1 , wherein the zone is formed from a washcoat that has a viscosity in the range of 100-750 centipoise (cp).
9. The zoned catalyst composite of claim 1 , wherein the zone is formed from a washcoat that has a yield point in the range of 1.5-10.0.
10. The zoned catalyst composite of claim 1 , wherein the zone is formed from a washcoat that comprises the catalytic material in combination with a rheology system having one or more organic compounds comprising a polymeric thickener, a surfactant, and/or a dispersant.
11. The zoned catalyst composite of claim 10 , wherein the rheology system comprises a polymeric thickener, a surfactant, and a dispersant.
12. The zoned catalyst composite of claim 1 , wherein the zone is formed from a washcoat loading in the range of 0.10 to 1.0 g/in 3 .
13. The zoned catalyst composite of claim 1 , wherein the zone comprises a mean particle size in the range of 5 to 20 μm.
14. The zoned catalyst composite of claim 1 , wherein the distance of the zone from the one end of the carrier varies in the range of 0 to 15% from passage-to-passage.
15. The zoned catalyst composite of claim 1 , wherein for each passage, the concentration of active components in the catalytic material of the zone at the one end of the carrier as compared the concentration at the end of the zone varies in an amount of not more than 10%.
16. The zoned catalyst composite of claim 1 , wherein for each passage, the thickness of the zone at the one end of the carrier as compared to the thickness at the end of the zone varies in an amount of not more than 15%.
17. A system for treatment of an internal combustion engine exhaust stream including hydrocarbons, carbon monoxide, and other exhaust gas components, the emission treatment system comprising:
an exhaust conduit in fluid communication with the internal combustion engine via an exhaust manifold; and
the zoned catalyst composite according to claim 1 .
18. A method for treating exhaust gases comprising contacting a gaseous stream comprising hydrocarbons, carbon monoxide, and nitrogen oxides with the zoned catalyst composite according to claim 1 .
19. A method of making a zoned catalyst composite, the method comprising:
forming a shear thinning washcoat; and
dipping an inlet end of a monolithic carrier comprising a plurality of longitudinal passages into the washcoat to a depth to form an inlet zone that has a flat profile;
wherein at least one of the following conditions is met: (i) the distance of the zone from the inlet end of the carrier varies in the range of 0 to 15% from passage-to-passage; and (ii) for each passage, the thickness of the zone at the inlet end of the carrier as compared to the thickness at the end of the zone varies in an amount of not more than 15%.
20. The method of claim 19 further comprising after dipping, providing a gaseous pulse through the longitudinal passages to remove excess washcoat.
21. The method of claim 19 further comprising applying a vacuum pressure to the passages during the dipping step.