Water-based epoxy formulations for applied fireproofing
The present disclosure relates to coating compositions, kits, and methods of applying the same, for use with fireproofing materials. The coating compositions are effective to control the drying rate and shrinkage of fireproofing materials. The coating compositions are also able to be applied to fireproofing materials shortly after these materials have been applied to a substrate.
1. A method of coating comprising
(i) applying a coating of fireproofing material directly to a substrate, wherein the fireproofing material is a plaster-based or cement-based fireproofing comprising an inorganic binder and aggregate, and wherein the coating of fireproofing material has a water content of at least about 20 wt %;
(ii) applying a uniform coating of a coating composition directly to the coating of fireproofing material, wherein the coating of a coating composition has a thickness between 1 and 6 mils, and wherein the coating composition is a water-based epoxy composition comprising an epoxy resin, an aliphatic polyamine hardener, and water, and
(iii) applying a latex coating or caulk coating directly to the coating of a coating composition, wherein the latex coating comprises polymers or copolymers based on esters of acrylic acid or vinyl alcohol, and wherein the caulk composition comprises silicone, polyurethane, polysulfide, polyacrylic polymers or polyacrylic copolymers.
2. The method of claim 1 , wherein the coating of fireproofing material has a thickness of 1 inch or more.
3. The method of claim 1 , wherein the uniform coating of a coating composition is directly applied to the coating of fireproofing material within 7 days after the fireproofing material is directly applied to the substrate.
4. The method of claim 3 , wherein the uniform coating of a coating composition is directly applied to the coating of fireproofing material within 5 days after the fireproofing material is directly applied to the substrate.
5. The method of claim 4 , wherein the uniform coating of a coating composition is directly applied to the coating of fireproofing material within 3 days after the fireproofing material is directly applied to the substrate.
6. The method of claim 5 , wherein the uniform coating of a coating composition is directly applied to the coating of fireproofing material within 48 hours after the fireproofing material is directly applied to the substrate.
7. The method of claim 6 , wherein the uniform coating of a coating composition is directly applied to the coating of fireproofing material within 24 hours after the fireproofing material is directly applied to the substrate.
8. The method of claim 7 , wherein the uniform coating of a coating composition is directly applied to the coating of fireproofing material within 8 hours after the fireproofing material is directly applied to the substrate.
9. The method of claim 8 , wherein the uniform coating of a coating composition is directly applied to the coating of fireproofing material within 4 hours after the fireproofing material is directly applied to the substrate.
10. The method of claim 9 , wherein the uniform coating of a coating composition is directly applied to the coating of fireproofing material within 1 hour after the fireproofing material is directly applied to the substrate.
11. An article produced by the method of claim 1 .