The invention relates, generally, to porous absorbent materials which are suitable for packing antrums or other cavities of the human or animal body. More particularly, it relates to hydrophilic biodegradable foams, which may be used e.g. in the form of a plug or tampon, for instance for controlling bleeding, wound closure, prevent tissue adhesion and/or support tissue regeneration. The invention provides an absorbent foam, suitable for packing antrums or other cavities of the human or animal body, comprising a biodegradable synthetic polymer, which polymer preferably comprises —C(O)—O— groups in the backbone of the polymer, for instance polyurethane and/or polyester units combined with polyethers.
1. A nasal packing comprising a phase-separated polymer including an amorphous segment and a crystalline segment, said polymer having the formula:
—[R-Q 1 [—R′—Z 1 —[R″—Z 2 —R′—Z 3 ] p —R″—Z 4 ] q —R′-Q 2 ]- n (I),
wherein:
the amorphous segment comprises R, and at least one R comprises the reaction product of a polyethylene glycol initiator having a number average molecular weight of 600 to 2000 g/mol, lactide, and ε-caprolactone, such that said at least one R comprises a first polyester segment based on lactide and ε-caprolactone, a central hydrophilic segment based on polyethylene glycol, and a second polyester segment based on lactide and ε-caprolactone, wherein said at least one R comprises:
polyethylene glycol in a content of 10-60 wt. %, and
lactide and ε-caprolactone in a content of 5-60 wt. %,
R′ and R″ are independently C 2 -C 8 alkylene,
Z 1 -Z 4 are each urethane,
Q 1 and Q 2 are each urethane,
n is an integer from 5-500,
p and q are both 1,
wherein said nasal packing has a complete fragmentation time ranging from 1 to 10 days.
2. The nasal packing according to claim 1 , wherein R′ is (CH 2 ) 4 , R″ is (CH 2 ) 4 , or both R′ and R″ are (CH 2 ) 4 .
3. The nasal packing according to claim 1 , wherein said at least one R comprises lactide and ε-caprolactone in a content of 20-50 wt. %.
4. The nasal packing according to claim 1 , wherein said at least one R comprises lactide and ε-caprolactone in a 1:1 molar ratio.
5. The nasal packing according to claim 1 , characterized in that said nasal packing has a swellability of less than 5%, and a fluid absorption capacity of 1500-2500% based on a dry weight of said nasal packing.
6. The nasal packing according to claim 1 , characterized in that said nasal packing has a fluid absorption capacity of 0.5-0.99 g/cm 3 or a density of 0.01-0.2 g/cm 3 .
7. The nasal packing according to claim 1 , wherein said at least one R comprises polyethylene glycol in a content of 20-50 wt. %.
8. The nasal packing according to claim 1 , wherein said at least one R has a molecular weight between 1,000 and 4,000 and comprises about 25 w betide, about 25 wt. % ε-caprolactone, and about 50 wt. % of polyethyleneglycol.
9. The nasal packing according to claim 1 , wherein said nasal packing has a porosity ranging from 85 to 99%.
10. The nasal packing according to claim 1 further comprising a drug substance.
11. The nasal packing according to claim 1 further comprising a haemostatic component.
12. The nasal packing according to claim 1 , wherein said nasal packing has an initial elastic modulus of from 30-120 MPa and a tensile strength of 10-45 MPa.
13. The nasal packing according to claim 1 , wherein said nasal packing has an initial elongation at break from 500-1200%.
14. The nasal packing according to claim 1 , wherein the nasal packing has a thickness (h) of 10-15 mm; a width of 15-20 mm; and a length (l) of 35 to 85 mm.
15. A nasal packing comprising a phase-separated polymer including an amorphous segment and a crystalline segment, said polymer having the formula:
—[R-Q 1 [—R′—Z 1 —[R″—Z 2 —R′—Z 3 ] p —R″—Z 4 ] q —R′-Q 2 ]- n (I),
wherein:
the amorphous segment comprises R, and at least one R comprises the reaction product of a polyethylene glycol initiator having a number average molecular weight of 600 to 2000 g/mol, lactide, and ε-caprolactone, such that said at least one R comprises a first polyester segment based on lactide and ε-caprolactone, a central hydrophilic segment comprising polyethylene glycol, and a second polyester segment based on lactide and ε-caprolactone, wherein said at least one R comprises:
polyethylene glycol in a content of 10-60 wt. %, and
lactide and ε-caprolactone in a content of 5-60 wt. %,
R′ and R″ are independently C 2 -C 8 alkylene, optionally substituted with C 1 -C 10 alkyl or C 1 -C 10 alkyl groups substituted with protected S, N, P or O moieties and/or comprising S, N, P or O in the alkylene chain;
Z 1 -Z 4 are independently amide, urea or urethane,
Q 1 and Q 2 are independently urea, urethane, amide, carbonate, ester or anhydride,
n is an integer from 5-500,
p and q are both 1,
wherein said nasal packing has a complete fragmentation time ranging from 1 to 10 days.
16. The nasal packing according to claim 15 , wherein Z 1 -Z 4 and Q 1 and Q 2 are each urethane.
17. The nasal packing according to claim 15 , wherein said at least one R comprises lactide and ε-caprolactone in a content of 20-50 wt. %.
18. The nasal packing according to claim 15 , wherein the nasal packing has a thickness (h) of 10-15 mm; a width of 15-20 mm; and a length (l) of 35 to 85 mm.
19. The nasal packing according to claim 15 , wherein said at least one R comprises polyethylene glycol in a content of 20-50 wt. %.