View Patent ↗Disclosed are asphalts that are suitable for making shingles and other roofing material, i.e., coating asphalts, from harder paving asphalts, without oxidation of the paving asphalts. This is achieved by using various additives, including polyethylene waxes, low density and high density polyethylene materials, hard paraffin polyethylene, Sasol waxes, that are made using the Fischer-Tropsch process, and thermoplastic polyolefins that reduce brittleness at cold temperatures.
1. A method of modifying a non-coating grade asphalt to produce a coating grade asphalt without oxidation of said non-coating grade asphalt comprising:
heating said non-coating grade asphalt to a melting temperature in a mixing chamber to produce a melted non-coating grade asphalt, said non-coating grade asphalt comprising:
a blend of AC-20 asphalt and 10% to 20% of 0-Pen asphalt;
mixing said melted non-coating grade asphalt with additive to create a mixture which improves properties of said non-coating grade asphalt to properties of a coating grade asphalt, without oxidizing said non-coating grade asphalt, said additives comprising:
a fine crystalline, long chain, aliphatic polymethylene hydrocarbon wax having a concentration of approximately 10% to 20% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture to increase flexibility at low temperatures.
2. A method of modifying a non-coating grade asphalt to produce a coating grade asphalt without oxidation of said non-coating grade asphalt comprising:
heating said non-coating grade asphalt to a melting temperature in a mixing chamber to produce a melted non-coating grade asphalt, said non-coating grade asphalt comprising:
a blend of AC-20 asphalt and 10% to 20% of 0-Pen asphalt;
mixing said melted non-coating grade asphalt with additives to create a mixture which improves properties of said non-coating grade asphalt to properties of a coating grade asphalt, without oxidizing said non-coating grade asphalt, said additives comprising:
a polyethylene synthetic wax having a concentration of 10% to 15% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
3. A method of modifying a non-coating grade asphalt to produce a coating grade asphalt without oxidation of said non-coating grade asphalt comprising:
heating said non-coating grade asphalt to a melting temperature in a mixing chamber to produce a melted non-coating grade asphalt, said non-coating grade asphalt comprising:
a blend of AC-20 asphalt and 10% to 30% 0-Pen asphalt;
mixing said melted non-coating grade asphalt with additives to create a mixture which improves properties of said non-coating grade asphalt to properties of a coating grade asphalt, without oxidizing said non-coating grade asphalt, said additives comprising:
a synthetic wax produced by de-polymerization of polyethylene or polypropylene having a concentration of approximately 10% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
4. A method of modifying a non-coating grade asphalt to produce a coating grade asphalt without oxidation of said non-coating grade asphalt comprising:
heating said non-coating grade asphalt to a melting temperature in a mixing chamber to produce a melted non-coating grade asphalt, said non-coating grade asphalt comprising:
a blend of AC-20 asphalt and approximately 20% 0-Pen asphalt;
mixing said melted non-coating grade asphalt with additives to create a mixture which improves properties of said non-coating grade asphalt to properties of a coating grade asphalt, without oxidizing said non-coating grade asphalt, said additives comprising:
a synthetic wax produced by de-polymerization of low density polyethylene that has a concentration of approximately 10% to 15% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
5. A method of modifying a non-coating grade asphalt to produce a coating grade asphalt without oxidation of said non-coating grade asphalt comprising:
heating said non-coating grade asphalt to a melting temperature in a mixing chamber to produce a melted non-coating grade asphalt, said non-coating grade asphalt comprising:
a blend of AC-20 asphalt and approximately 20% 0-Pen asphalt;
mixing said melted non-coating grade asphalt with additives to create a mixture which improves properties of said non-coating grade asphalt to properties of a coating grade asphalt, without oxidizing said non-coating grade asphalt, said additive comprising:
a synthetic wax, produced by de-polymerization of high density polyethylene that has a concentration of approximately 10% to 15% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
6. A method of modifying a non-coating grade asphalt to produce a coating grade asphalt without oxidation of said non-coating grade asphalt comprising:
heating said non-coating grade asphalt to a melting temperature in a mixing chamber to produce a melted non-coating grade asphalt, said non-coating grade asphalt comprising:
a blend of AC-20 asphalt and approximately 25% 0-Pen asphalt;
mixing said melted non-coating grade asphalt with additives to create a mixture that improves properties of said non-coating grade asphalt to properties of a coating grade asphalt, without oxidizing said non-coating grade asphalt, said additives comprising:
a synthetic wax produced by de-polymerization of high density polyethylene that has a concentration of approximately 10% of said mixture;
naphthenic resid having a concentration of approximately 10% of said mixture.
7. A coating grade asphalt suitable for making asphalt roofing shingles comprising:
a non-coating grade asphalt, that has not been oxidized, comprising:
a blend of AC-20 asphalt and 10% to 20% of 0-Pen asphalt;
at least one additive mixed with said non-coating grade asphalt to modify said non-coating grade asphalt, without oxidizing said non-coating grade asphalt, to create a mixture that has properties of a coating grade asphalt, said at least one additive comprising:
a fine crystalline, long chain, aliphatic polymethylene hydrocarbon wax, that is made using a Fischer-Tropsch process, said fine crystalline, long chain, aliphatic polymethylene hydrocarbon wax having a concentration of approximately 10% to 20% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture which increases flexibility at low temperatures.
8. A coating grade asphalt suitable for making asphalt roofing shingles comprising:
a non-coating grade asphalt, that has not been oxidized, comprising:
a blend of AC-20 asphalt and 5% to 20% of 0-Pen asphalt;
at least one additive mixed with said non-coating grade asphalt to modify said non-coating grade asphalt, without oxidizing said non-coating grade asphalt, to create a mixture that has properties of a coating grade asphalt, said at least one additive comprising:
a polyethylene synthetic wax having a concentration of 10% to 15% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
9. A coating grade asphalt suitable for making asphalt roofing shingles comprising:
a non-coating grade asphalt, that has not been oxidized, comprising:
a blend of AC-20 asphalt and 10% to 20% of 0-Pen asphalt;
at least one additive mixed with said non-coating grade asphalt to modify said non-coating grade asphalt, without oxidizing said non-coating grade asphalt, to create a mixture that has properties of a coating grade asphalt, said at least one additive comprising:
a polyethylene synthetic wax having a concentration of 10% to 15% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
10. A coating grade asphalt suitable for making asphalt roofing shingles comprising:
a non-coating grade asphalt, that has not been oxidized, comprising:
a blend of AC-20 asphalt and 10% to 30% of 0-Pen asphalt;
at least one additive mixed with said non-coating grade asphalt to modify said non-coating grade asphalt, without oxidizing said non-coating grade asphalt, to create a mixture that has properties of a coating grade asphalt, said at least one additive comprising:
a synthetic wax, produced by de-polymerization of polyethylene or polypropylene, having a concentration of approximately 10% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
11. A coating grade asphalt suitable for making asphalt roofing shingles comprising:
a non-coating grade asphalt, that has not been oxidized, comprising:
a blend of AC-20 asphalt and approximately 20% of 0-Pen asphalt;
at least one additive mixed with said non-coating grade asphalt to modify said non-coating grade asphalt, without oxidizing said non-coating grade asphalt, to create a mixture that has properties of a coating grade asphalt, said at least one additive comprising:
a synthetic wax, produced by de-polymerization of low density polyethylene that has a concentration of approximately 10% to 15% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
12. A coating grade asphalt suitable for making asphalt roofing shingles comprising:
a non-coating grade asphalt, that has not been oxidized, comprising:
a blend of AC-20 asphalt and approximately 20% of 0-Pen asphalt;
at least one additive mixed with said non-coating grade asphalt to modify said non-coating grade asphalt, without oxidizing said non-coating grade asphalt, to create a mixture that has properties of a coating grade asphalt, said at least one additive comprising:
a synthetic wax, produced by de-polymerization of high density polyethylene, that has a concentration of approximately 10% to 15% of said mixture;
a thermoplastic polyolefin having a concentration of approximately 3% of said mixture.
13. A coating grade asphalt suitable for making asphalt roofing shingles comprising:
a non-coating grade asphalt, that has not been oxidized, comprising:
a blend of AC-20 asphalt and approximately 25% of 0-Pen asphalt;
at least one additive mixed with said non-coating grade asphalt to modify said non-coating, grade asphalt, without oxidizing said non-coating grade asphalt, to create a mixture that has properties of a coating grade asphalt, said at least one additive comprising:
a synthetic wax, produced by de-polymerization of high density polyethylene that has a concentration of approximately 10% of said mixture;
naphthenic resid having a concentration of approximately 10% of said mixture.