Thermal propagation mitigation for HV battery modules
A high voltage battery module includes a plurality of battery cells, a plurality of cooling fins dispersed between the battery cells, and a frame for holding the plurality of battery cells and the plurality of fins. An intumescent layer is proximate to at least one battery module component selected from the battery cells, the plurality of cooling fins, and the frame. The intumescent layer includes sodium silicate having formula Na 2 SiO 3 , pentaerythitol, a resin that is cross-linked by melamine, boron nitride particles, and triammonium phosphate.
1. A high voltage battery module comprising:
a plurality of battery cells;
a plurality of cooling fins dispersed between the plurality of battery cells;
a frame for holding the plurality of battery cells and the plurality of cooling fins; and
an intumescent layer proximate to at least one battery module component, the intumescent layer including:
sodium silicate having a formula Na 2 SiO 3 ;
pentaerythritol;
a resin that is cross-linked by melamine, wherein the resin includes a polyester resin or an epoxy resin;
boron nitride particles; and
triammonium phosphate;
wherein the sodium silicate is present in an amount from about 25 weight percent to 50 weight percent of the total weight of the intumescent layer, the pentaerythritol is present in an amount from about 2 weight percent to 20 weight percent of the total weight of the intumescent layer, the resin cross-linked by melamine is present in an amount from about 20 weight percent to 60 weight percent of the total weight of the intumescent layer, the boron nitride particles are present in an amount from about 2 weight percent to 30 weight percent of the total weight of the intumescent layer, and the triammonium phosphate is present in an amount from about 0.1 weight percent to 3 weight percent of the total weight of the intumescent layer.
2. The high voltage battery module of claim 1 wherein the boron nitride particles are nanostructured boron nitride particles having an average spatial dimension from about 20 to 100 nanometers.
3. The high voltage battery module of claim 1 wherein the sodium silicate is present in an amount from about 30 weight percent to 35 weight percent of the total weight of the intumescent layer, the pentaerythritol is present in an amount from about 5 weight percent to 10 weight percent of the total weight of the intumescent layer, the resin cross-linked by melamine is present in an amount from about 30 weight percent to 40 weight percent of the total weight of the intumescent layer, the boron nitride is present in an amount from about 5 weight percent to 20 weight percent of the total weight of the intumescent layer, and the triammonium phosphate is present in an amount from about 0.5 weight percent to 1 weight percent of the total weight of the intumescent layer.
4. The high voltage battery module of claim 1 wherein the intumescent layer further includes a filler.
5. The high voltage battery module of claim 1 wherein the intumescent layer is a gel or foam.
6. The high voltage battery module of claim 1 wherein at least one cooling fin is coated with or encapsulated by the intumescent layer.
7. The high voltage battery module of claim 1 wherein at least one battery cell is coated with or encapsulated by the intumescent layer.
8. The high voltage battery module of claim 1 further comprising foamed layers that are interposed between battery cells and cooling fins, the foamed layers being coated with the intumescent layer or encapsulated by the intumescent layer.
9. The high voltage battery module of claim 1 wherein the intumescent layer is a foamed layer that is interposed between battery cells and cooling fins.
10. The high voltage battery module of claim 1 wherein the frame is coated with or encapsulated by the intumescent layer.
11. A high voltage battery module comprising:
a plurality of battery modules;
a plurality of cooling fin assemblies dispersed between the plurality of battery modules, the plurality of cooling fin assemblies at least partially coated by an intumescent layer, the intumescent layer including:
sodium silicate in an amount from about 25 weight percent to 50 weight percent of the total weight of the intumescent layer;
pentaerythritol in an amount from about 2 weight percent to 20 weight percent of the total weight of the intumescent layer;
a resin that is cross-linked by melamine in an amount from about 20 weight percent to 60 weight percent of the total weight of the intumescent layer, the resin including a polyester resin or an epoxy resin;
boron nitride particles in an amount from about 2 weight percent to 30 weight percent of the total weight of the intumescent layer; and
triammonium phosphate in an amount from about 0.1 weight percent to 3 weight percent of the total weight of the intumescent layer.
12. The high voltage battery module of claim 11 wherein the boron nitride particles are nanostructured boron nitride particles having an average spatial dimension from about 20 nanometers to 100 nanometers.
13. The high voltage battery module of claim 11 wherein the sodium silicate is present in an amount from about 30 weight percent to 35 weight percent of the total weight of the intumescent layer, the pentaerythritol is present in an amount from about 5 weight percent to 10 weight percent of the total weight of the intumescent layer, the resin that is cross-linked by melamine is present in an amount from about 30 weight percent to 40 weight percent of the total weight of the intumescent layer, the boron nitride is present in an amount from about 5 weight percent to 20 weight percent of the total weight of the intumescent layer, and the triammonium phosphate is present in an amount from about 0.5 weight percent to 1 weight percent of the total weight of the intumescent layer.
14. The high voltage battery module of claim 11 wherein the intumescent layer further includes a filler.
15. The high voltage battery module of claim 11 wherein the cooling fin assemblies are encapsulated by the intumescent layer.
16. The high voltage battery module of claim 11 wherein the resin that is cross-linked by melamine is an alkyd resin.
17. A high voltage battery module comprising:
a plurality of battery cells;
a plurality of cooling fins dispersed between the plurality of battery cells;
a frame for holding the plurality of battery cells and the plurality of cooling fins; and
an intumescent layer proximate to at least one battery module component, the intumescent layer consisting of:
sodium silicate having a formula Na 2 SiO 3 ;
pentaerythritol;
a resin that is cross-linked by melamine;
boron nitride particles; and
triammonium phosphate;
wherein the sodium silicate is present in an amount from about 25 weight percent to 50 weight percent of the total weight of the intumescent layer, the pentaerythritol is present in an amount from about 2 weight percent to 20 weight percent of the total weight of the intumescent layer, the resin cross-linked by melamine is present in an amount from about 20 weight percent to 60 weight percent of the total weight of the intumescent layer, the boron nitride particles are present in an amount from about 2 weight percent to 30 weight percent of the total weight of the intumescent layer, and triammonium phosphate is present in an amount from about 0.1 weight percent to 3 percent of the total weight of the intumescent layer.
18. The high voltage battery module of claim 17 wherein the resin that is cross-linked by melamine includes a polyester resin or an epoxy resin.