Method of making a contact lens
View Patent ↗A method of making a contact lens comprising the steps of reacting in a mold a polymerizable formulation comprising at least one fluorine-containing silicone monomer at least one non-fluorine-containing silicone monomer and at least one hydrophilic monomer to form a contact lens, subjecting the contact lens to one or more solvent extraction steps to remove impurities, oligomers and unreacted monomers and hydrate the contact lens, wherein all of the solvent extraction steps are undertaken using an aqueous solvent.
1. A contact lens comprising a reaction product of a polymerisable formulation comprising:
(i) from 20 to 35 weight percent of at least one fluorine-containing silicone monomer having the formula:
wherein n is from 1 to 10;
(ii) from 15 to 35 weight percent of at least one non-fluorine containing silicone monomer;
(iii) from 25 to 60 weight percent N-vinyl pyrrolidone or N-methyl-N-vinyl acetamide;
(iv) from 2 to 10 weight percent 2-hydroxyethyl methacrylate,
wherein the total amount of components (i) and (ii) is less than 50 weight percent.
2. A contact lens comprising a reaction product of a polymerisable formulation comprising:
(i) from 20 to 35 weight percent of at least one fluorine-containing silicone monomer having the formula:
wherein each n is independently from 1 to 10;
(ii) from 8 to 35 weight percent of at least one non-fluorine containing silicone monomer;
(iii) from 25 to 60 weight percent N-vinyl pyrrolidone or N-methyl-N-vinyl acetamide;
(iv) from 2 to 10 weight percent 2-hydroxyethyl methacrylate,
wherein the total amount of components (i) and (ii) is less than 55 weight percent.
3. A contact lens as claimed in claim 1 or claim 2 wherein the formulation additionally comprises at least one cross-linker.
4. A contact lens as claimed in claim 3 , wherein the cross-linker is selected from the group consisting of allyl (meth)acrylate, C 2-6 alkylene glycol di(meth)acrylate, poly(C 2-6 alkylene)glycol di(meth)acrylate, divinyl ether, divinyl sulfone, di- and trivinylbenzene, trimethylolpropane tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, bisphenol A di(meth)acrylate, triallyl cyanuronate, methylenebis(meth)acrylamide, triallyl phthalate, diallyl phthalate, 1,3-Bis(methacrylamidopropyl)-1,1,3,3-tetrakis(trimethylsiloxy)disiloxane, 1,3-Bis(N-methylmethacrylamidopropyl)-1,1,3,3-tetrakis(trimethylsiloxy)disiloxane, 1,3-Bis(methacrylamidopropyl)-1,1,3,3-tetrakis(trimethylsiloxy)disiloxane, 1,3-Bis(acrylamidopropyl)-1,1,3,3-tetrakis(trimethylsiloxy)disiloxane, 1,3-Bis(methacryloxyethylureidopropyl)-1,1,3,3-tetrakis(trimethylsiloxy)disiloxane and mixtures thereof.
5. A contact lens as claimed in claim 4 , wherein the cross-linker comprises tetraethyleneglycol dimethacrylate.
6. A contact lens as claimed in claim 1 or claim 2 wherein the formulation additionally comprises a non-silicon containing hydrophobic monomer.
7. A contact lens as claimed in claim 6 , wherein the hydrophobic monomer is selected from the group consisting of methyl acrylate, ethyl acrylate, propyl acrylate, isopropyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl acrylate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl valerate, styrene, chloroprene, vinyl chloride, vinylidene chloride, acrylonitrile, 1-butene, butadiene, methacrylonitrile, vinyltoluene, vinyl ethyl ether, perfluorohexylethylthiocarbonylaminoethyl methacrylate, isobornyl methacrylate, trifluoroethyl methacrylate, hexafluoroisopropyl methacrylate, tetrafluoropropyl methacrylate, hexafluorobutyl methacrylate and mixtures thereof.
8. A contact lens as claimed in claim 1 or claim 2 , wherein the formulation additionally comprises N,N-dimethylacrylamide in an amount of from 3 to 10 weight percent.
9. A contact lens as claimed in claim 1 or claim 2 , wherein the non-fluorine containing silicone monomer is selected from the group consisting of tris(trimethylsilyloxy)silylpropyl methacrylate (TRIS), 3-methacryloxypropyldimethyl siloxanes (MAPDMS), 3-methacryloxy propylpentamethyldisiloxane, bis(methacryloxypropyl)tetramethyldisiloxane, N[tris(trimethylsiloxy)silylpropyl]methacrylamide (TSMAA), N[tris(trimethylsiloxy)silylpropyl]acrylamide, N[tris(trimethylsiloxy)silylpropyl]methacryloxyethylcarbamate, N[tris(dimethylpropylsiloxy)silylpropyl]methacrylamide, N[tris(dimethylphenylsiloxy)silylpropyl]methacrylamide, N[tris(trimethylsiloxy)silylpropyl]methacryloxyglycerylcarbamate, N[tris(dimethylethylsiloxy)silylpropyl]methacrylamide, N[tris(trimethylsiloxy)silylpropyl]methacryloxyacetamide, and N[tris(trimethylsiloxy)silylpropyl]methacryloxymethyl dimethylacetamide and mixtures thereof.
10. A contact lens as claimed in claim 9 , wherein the non-fluorine containing silicone monomer is tris(trimethylsilyloxy)silylpropylmethacrylate.
11. A contact lens as claimed in claim 1 or claim 2 , wherein the modulus of the lens is less than 0.6 MPa.
12. A contact lens as claimed in claim 1 or claim 2 , wherein the oxygen permeability of the lens is greater than 60 barrers.
13. A contact lens as claimed in claim 1 or claim 2 , wherein the bulk water content of the lens is from 35 to 60%.
14. A contact lens as claimed in claim 1 or claim 2 , wherein the centre thickness is from 50 to 100 microns.