LINOLEUM COMPOSITION WITH HYDROPHOBIC ADDITIVE
A linoleum composition comprising Bedford cement as a binder, wood flour as a filler, and wax in an amount effective to provide the wood flour filler with hydrophobic properties.
1 . A linoleum composition comprising:
a binder comprising Bedford cement;
a filler comprising wood flour; and
a wax present in an amount ranging from 0.1 wt. % to 0.5 wt. % based on the weight of the linoleum composition, thereby providing the wood flour filler with hydrophobic properties.
2 . The linoleum composition of claim 1 , wherein the wax is present in an amount of from 0.2 to 0.4 wt % based on the weight of the linoleum composition.
3 . The linoleum composition of claim 1 , wherein the wax has a congealing point of from 54 to 56° C.
4 . The linoleum composition of any one of claim 1 , wherein the wood flour is present in an amount of from 35 to 45 wt % based on the weight of the linoleum composition.
5 . The linoleum composition of claim 1 , wherein the wood flour has a particle size fraction 80-160 μm: 40-90%, fraction <80 μm 10-50%.
6 . The linoleum composition of claim 1 , wherein the filler further comprises limestone in an amount of from 5 wt. % to 30 wt. % based on the weight of the linoleum composition.
7 . The linoleum composition of claim 1 , wherein the Bedford cement is present in an amount of from 30 to 45 wt % based on the weight of the linoleum composition.
8 . The linoleum composition of claim 1 , further comprising aluminium trihydroxide in an amount of from 5 to 15 wt % based on the weight of the linoleum composition.
9 . The linoleum composition of claim 1 , further comprising one or more pigments in an amount of up to 5 wt % based on the weight of the linoleum composition.
10 . The linoleum composition of claim 1 , further comprising zinc oxide in an amount of from 0.1. to 1 wt % based on the weight of the linoleum composition.
11 . A flooring material having a front major surface and a rear major surface opposite the front major surface, the flooring material comprising a linoleum composition layer that comprises:
a binder comprising Bedford cement;
a filler comprising wood flour; and
a wax present in an amount ranging from 0.1 wt. % to 0.5 wt. % based on the weight of the linoleum composition.
12 . The flooring material of claim 11 , wherein the flooring material is a layer element selected from a tile, sheet and web.
13 . The flooring material of claim 11 further comprising a carrier scrim located at the rear major surface of the flooring material.
14 . The flooring material of claim 13 , wherein the carrier scrim comprises material including a mixture of polymer weft fibres and glass warp fibers, the polymer fibres comprising at least one of polyester fibers and polyethylene terephthalate (PET) fibers.
15 . The flooring material of claim 11 further comprising a coating applied to the front major surface of the flooring material, the coating comprising a polyurethane resin layer having a thickness ranging from 10 to 30 microns.
16 . The flooring material of claim 11 , wherein the linoleum composition layer of the flooring material has a thickness ranging from 1 mm to 6 mm.
17 . A flooring material having a multi-layer structure comprising a first linoleum composition layer and a second linoleum composition layer, wherein at least one of the first linoleum composition layer and the second linoleum composition layer comprises:
a binder comprising Bedford cement;
a filler comprising wood flour; and
a wax present in an amount ranging from 0.1 wt. % to 0.5 wt. % based on the weight of each of the first or the second linoleum composition layers;
wherein the first linoleum composition layer and the second linoleum composition layers are bonded together at an interface therebetween.
18 . The flooring material of claim 17 , wherein the first linoleum composition layer comprises the wax and the second linoleum composition layer is substantially free of the wax.
19 . The flooring material of claim 17 , wherein the first linoleum composition layer has a thickness ranging from 0.5 mm to 3 mm.
20 . The flooring material of claim 17 , wherein the second linoleum composition layer has a thickness ranging from 0.5 mm to 4 mm.