Ceramic honeycomb structure and its production method
A method for producing a honeycomb-shaped ceramic structure by extrusion-molding a moldable material including a cordierite-forming material and a pore-forming material, wherein the cordierite-forming material contains 15-25% by mass of silica having an average particle size of 20-30 μm, with 5% or less by mass of particles having particle sizes of 10 μm or less and 5% or less by mass of particles having particle sizes of 100 μm or more, a particle size distribution deviation SD of 0.5 or less, and sphericity of 0.5 or more, and wherein the pore-forming material is present in an amount of 5-40% by mass based on the cordierite-forming material and has an average particle size of 15-50 μm, with 10% or less by mass of particles having particle sizes of 5 μm or less and 5% or less by mass of particles having particle sizes of 80 μm or more.
1. A method for producing a honeycomb-shaped ceramic structure by extrusion-molding a moldable material comprising a cordierite-forming material and a pore-forming material,
said cordierite-forming material containing 15-25% by mass of silica;
said silica having an average particle size of 20-30 μm with 5% or less by mass of particles having particle sizes of 10 μm or less, and 5% or less by mass of particles having particle sizes of 100 μm or more, a particle size distribution deviation SD of 0.5 or less, and sphericity of 0.5 or more;
the amount of said pore-forming material being 5-40% by mass based on the cordierite-forming material; and
said pore-forming material having an average particle size of 15-50 μm with 10% or less by mass of particles having particle sizes of 5 μm or less, and 5% or less by mass of particles having particle sizes of 80 μm or more, a particle size distribution deviation SD=log(d 80 )−log(d 20 ) of 0.5 or less, and sphericity of 0.5 or more, wherein d 20 represents a particle size (m) at a cumulative volume corresponding to 20% of the total volume, and d 80 similarly represents a particle size (μm) at a cumulative volume corresponding to 80% of the total volume, on a curve showing the relation between a particle size and a cumulative volume of particles having a particular particle size or less, and d 20 <d 80 .
2. The method for producing a ceramic honeycomb structure according to claim 1 , wherein said pore-forming material is a porous polymer, and wherein said pore-forming material particles contain 30% or more and less than 50% of voids.
3. The method for producing a ceramic honeycomb structure according to claim 2 , wherein 80% or more of voids in said pore-forming material particles contain water.
4. The method for producing a ceramic honeycomb structure according to claim 3 , wherein said cordierite-forming material contains 40-43% by mass of talc, and wherein said talc has an average particle size of 1-10 μm, d 90 of 30 μm or less, wherein d 90 is a particle size at a cumulative volume corresponding to 90% of the total volume on a curve showing the relation between a particle size and a cumulative volume of particles having a particular particle size or less, and a particle size distribution deviation SD of 0.7 or less.
5. The method for producing a ceramic honeycomb structure according to claim 4 , wherein said talc particles have a morphology index (indicating the degree of platelikeness) of 0.77 or more.
6. The method for producing a ceramic honeycomb structure according to claim 3 , wherein said cordierite-forming material contains talc particles, and
wherein said talc particles have a morphology index (indicating the degree of platelikeness) of 0.77 or more.
7. The method for producing a ceramic honeycomb structure according to claim 2 , wherein said cordierite-forming material contains 40-43% by mass of talc, and wherein said talc has an average particle size of 1-10 μm, d 90 of 30 μm or less, wherein d 90 is a particle size at a cumulative volume corresponding to 90% of the total volume on a curve showing the relation between a particle size and a cumulative volume of particles having a particular particle size or less, and a particle size distribution deviation SD of 0.7 or less.
8. The method for producing a ceramic honeycomb structure according to claim 7 , wherein said talc particles have a morphology index (indicating the degree of platelikeness) of 0.77 or more.
9. The method for producing a ceramic honeycomb structure according to claim 2 , wherein said cordierite-forming material contains talc particles, and
wherein said talc particles have a morphology index (indicating the degree of platelikeness) of 0.77 or more.
10. The method for producing a ceramic honeycomb structure according to claim 1 , wherein said cordierite-forming material contains 40-43% by mass of talc, and wherein said talc has an average particle size of 1-10 d 90 of 30 μm or less, wherein d 90 is a particle size at a cumulative volume corresponding to 90% of the total volume on a curve showing the relation between a particle size and a cumulative volume of particles having a particular particle size or less, and a particle size distribution deviation SD of 0.7 or less.
11. The method for producing a ceramic honeycomb structure according to claim 10 , wherein said talc particles have a morphology index (indicating the degree of platelikeness) of 0.77 or more.
12. The method for producing a ceramic honeycomb structure according to claim 1 , wherein said cordierite-forming material contains talc particles, and
wherein said talc particles have a morphology index (indicating the degree of platelikeness) of 0.77 or more.