Fin stock material
View Patent ↗A fin stock material from an 3xxx-series aluminum alloy and including at least 0.5% to 2.0% Mn, and furthermore a purposive addition of one or more wetting elements selected from the group of: Bi 0.03% to 0.5%, Pb 0.03% to 0.5%, Sb 0.03% to 0.5%, Li 0.03% to 0.5%, Se 0.03% to 0.5%, Y 0.03% to 0.05%, Th 0.03% to 0.05%, and the sum of these elements being 0.5% or less, with the remainder including aluminum and tolerable impurities. Also provided is a method for manufacturing a heat exchanger assembly incorporating such a fin stock material.
1. A brazed assembly comprising a plurality of substantially parallel fluid-carrying tubes and a plurality of fins; said fins being in thermal communication with said plurality of fluid-carrying tubes and structured to transfer heat away therefrom, said plurality of fins consisting of a fin stock material from an 3xxx-series aluminium alloy and comprising by weight
Mn 0.5 to 2.0%
Si 0.5% to 1.5%
Fe 0 to 1.8%
Zn 0 to 2.5%
Mg 0 to 0.5%
Cu 0 to 0.4%, and
furthermore a purposive addition of Bi 0.03% to 0.5% as wetting agent, with the remainder comprising aluminium and tolerable impurities, wherein said fin stock material does not have any additional metallic layers such that the wetting agent is diffused to the outer surface of the fin stock material when the fin stock material is brazed; and
wherein the fin stock material at final gauge has a thickness of 0.05 to 0.15 mm.
2. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises further one or more elements selected from the group of up to 0.25% Zr, up to 0.25% Cr, up to 0.25% V, up to 0.25% Ti, up to 0.20% In, up to 0.3% Ni.
3. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises Bi in a range of 0.03% to 0.35%.
4. A brazed assembly according to claim 1 , wherein said aluminium alloy further comprises Mg in a range of 0.01% to 0.35%.
5. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises Mn in the range of 0.8% to 2.0%.
6. A brazed assembly according to claim 1 , and wherein said aluminium alloy comprises Fe in the range of 0.15% to 0.8%.
7. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises,
Mn 0.5% to 2.0%
Si 0.3% to 1.5%
Fe 0 to 1.8%
Zn 0 to 2.5%
Mg 0 to 0.5%
Cu 0 to 0.4%
Bi 0.03% to 0.5%,
optionally one or more elements selected from the group of up to about 0.25% Zr, up to about 0.25% Cr, up to about 0.25% V, up to about 0.25% Ti, up to about 0.20% In, up to about 0.3% Ni,
with the remainder comprising aluminium and tolerable impurities.
8. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises Cu up to 0.20%.
9. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises Cu at a level below 0.05%.
10. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises Zr in the range of 0.05% to 0.20%.
11. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises Zr in the range of 0.06% to 0.15%.
12. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises Ti in the range of up to 0.25%.
13. The brazed assembly according to claim 1 , wherein the brazed assembly is a heat exchanger.
14. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises,
Mn 0.5% to 2.0%
Si 0.3° A to 1.5%
Fe 0 to 1.8%
Zn 0.35 to 2.5%
Mg 0.01 to 0.35%
Cu 0 to 0.4%
Bi 0.03% to 0.5%,
In 0.01 to about 0.20%
Zr 0.05 to about 0.20%,
optionally one or more elements selected from the group of up to about 0.25% Cr, up to about 0.25% V, up to about 0.25% Ti, up to about 0.3% Ni, with the remainder comprising aluminium and tolerable impurities.
15. A brazed assembly according to claim 1 , wherein said aluminium alloy comprises,
Mn 0.5% to 2.0%
Si 0.3° A to 1.5%
Fe 0 to 1.8%
Zn 0 to 2.5%
Mg 0 to 0.5%
Cu 0 to 0.4%
Zr 0.05 to about 0.25%,
Cr 0 to about 0.25%,
Bi 0.03% to 0.5%,
Ti 0 to about 0.25%,
with the remainder comprising aluminium and tolerable impurities each up to 0.05%, total impurities 0.25% maximum.
16. A brazed assembly according to claim 1 , wherein in said fin stock material
Fe 0.2 to 0.8%
Mg 0.01 to 0.35%
Cu 0 to 0.2%
Cr 0 to 0.05%,
Bi 0.03% to 0.35%,
Ti 0.03 to 0.09%,
which is free of Na, Li, K and Ca, with the remainder comprising aluminium and tolerable impurities each up to 0.05%, total impurities 0.25% maximum.
17. A brazed assembly according to claim 1 , wherein said aluminium alloy consists of,
Mn 0.5% to 2.0%
Si 0.3° A to 1.5%
Fe 0 to 1.8%
Zn 0 to 2.5%
Mg 0 to 0.5%
Cu 0 to 0.4%
Zr 0.05 to about 0.25%,
Cr 0 to about 0.05%,
Bi 0.03% to 0.5%,
Ti 0 to about 0.25%
which is free of Na, Li, K and Ca, with the remainder comprising aluminium and tolerable impurities each up to 0.05%, total impurities 0.25% maximum.
18. A brazed assembly according to claim 1 , wherein in said fin stock material the level of Fe is 0.2 to 0.8%
the level of Mg is 0.01 to 0.35%
the level of Cu is 0 to 0.2%
the level of Cr is 0 to 0.05%,
the level of Bi is 0.03% to 0.35%,
which is free of Na, Li, K and Ca, with the remainder comprising aluminium and tolerable impurities each up to 0.05%, total impurities 0.25% maximum.
19. The brazed assembly according to claim 1 , wherein said fin stock material has an H1x or H2x temper.