Reinforced Window Profile
An extruded window profile includes metal inserts bound within and along the length of the profile through coextrusion of the profile and inserts through an extrusion die.
1 . An extruded window profile including a plurality of separate and integrated metal inserts within the entire length of the extruded window profile.
2 . The profile of claim 1 , wherein one or more of the inserts are bound by an adhesive to surrounding polyvinylchloride.
3 . The profile of claim 2 , wherein one or more of the inserts are aluminum.
4 . The profile of claim 1 , wherein one or more of the inserts are aluminum.
5 . The profile of claim 4 , wherein the profile comprises rigid polyvinylchloride.
6 . The profile of claim 1 , wherein the profile comprises rigid polyvinylchloride.
7 . The profile of claim 2 , wherein the profile comprises rigid polyvinylchloride.
8 . The profile of claim 7 wherein the adhesive is heat-activated.
8 . The profile of claim 3 , wherein the adhesive is heat-activated.
9 . The profile of claim 2 , wherein the adhesive is heat activated.
10 . A method of manufacturing an extruded window profile comprising extruding polyvinylchloride through a window profile extrusion die while continuously feeding one or more adhesive-coated aluminum reinforcing inserts through the die and in the surrounding polyvinylchloride that forms the outer surface of the extruded window profile.
11 . The method of claim 10 , wherein one or more aluminum inserts are flat.
12 . The method of claim 11 , further comprising feeding one or more aluminum inserts from a coil.
13 . The method of claim 10 , wherein the adhesive is heat-activated.
14 . The method of claim 13 , wherein some or all of an adhesive-coated surface of a reinforcing insert is heated prior to being fed through the die without fully heating the entirety of the reinforcing insert.
15 . The method of claim 11 , wherein the adhesive is heat-activated.
16 . The method of claim 15 , wherein some or all of an adhesive-coated surface of a reinforcing insert is heated prior to being fed through the die without fully heating the entirety of the reinforcing insert.
17 . The method of claim 16 , further comprising heating the aluminum reinforcing insert that is being heated in the range of from about 24 degrees Celsius to about 190 degrees Celsius prior to being fed through the die.
18 . The method of claim 16 , further comprising feeding the one or more inserts through the die at a speed of at least 40 inch/min.
19 . The method of claim 16 , further comprising heating the extrusion die in the range of from about 160 degrees Celsius to about 190 degrees Celsius.
20 . A window sash or frame comprising a continuously reinforced corner including mitered ends of adjacent extruded window profiles that each include a metal reinforcement insert with an end cut at a same angle as a mitered end of an insert's respective extruded window profile.