The present invention provides a method of making a substantially cylindrical insert by metal injection molding by providing a primer insert injection mold to form a substantially cylindrical metal primer insert, injection molding the metal injection molding feedstock into the primer insert injection mold to form a first substantially cylindrical metal primer insert having a first size; debinding the first substantially cylindrical metal primer insert to remove the first binding agent; and sintering the first substantially cylindrical metal primer insert to remove the second binding agent and form the substantially cylindrical metal primer insert having a second size.
1. A method of making a substantially cylindrical insert by injection molding comprising the steps of:
providing a primer insert injection mold to form a primer insert, wherein the primer insert mold comprises
a top surface opposite a bottom surface and a substantially cylindrical coupling element that extends from the bottom surface,
a primer recess in the top surface that extends toward the bottom surface,
a primer flash aperture positioned in the primer recess to extend through the bottom surface to the top surface,
a flash aperture groove positioned in the primer recess around the primer flash aperture, wherein the flash aperture groove is adapted to receive a polymer through the flash aperture during an overmolding process, and
a flange that extends circumferentially about an outer edge of the top surface, providing an injection molding feedstock;
injection molding the injection molding feedstock into the primer insert injection mold to form a primer insert; and
removing the primer insert from the primer insert injection mold.
2. The method of claim 1 , wherein the injection molding feedstock comprises a polymer or a powdered metal comprises stainless steel, brass, ceramic alloys.
3. The method of claim 2 , wherein the powdered metal comprises 102, 174, 201, 202, 300, 302, 303, 304, 308, 309, 316, 316L, 316Ti, 321, 405, 408, 409, 410, 415, 416, 416R, 420, 430, 439, 440, 446 or 601-665 grade stainless steel or Ti 6 Al 4 V.
4. The method of claim 2 , wherein the powdered metal comprises 2-16% Ni; 10-20% Cr; 0-5% Mo; 0-0.6% C; 0-6.0% Cu; 0-0.5% Nb+Ta; 0-4.0% Mn; 0-2.0% Si and the balance Fe.
5. The method of claim 2 , wherein the powdered metal comprises 2-6% Ni; 13.5-19.5% Cr; 0-0.10% C; 1-7.0% Cu; 0.05-0.65% Nb+Ta; 0-3.0% Mn; 0-3.0% Si and the balance Fe.
6. The method of claim 2 , wherein the powdered metal comprises 3-5% Ni; 15.5-17.5% Cr; 0-0.07% C; 3-5.0% Cu; 0.15-0.45% Nb+Ta; 0-1.0% Mn; 0-1.0% Si and the balance Fe.
7. The method of claim 2 , wherein the powdered metal comprises 10-14% Ni; 16-18% Cr; 2-3% Mo; 0-0.03% C; 0-2% Mn; 0-1% Si and the balance Fe.
8. The method of claim 2 , wherein the powdered metal comprises 12-14% Cr; 0.15-0.4% C; 0-1% Mn; 0-1% Si and the balance Fe.
9. The method of claim 2 , wherein the powdered metal comprises 16-18% Cr; 0-0.05% C; 0-1% Mn; 0-1% Si and the balance Fe.
10. The method of claim 2 , wherein the powdered metal comprises 3-12% aluminum, 2-8% vanadium, 0.1-0.75% iron, 0.1-0.5% oxygen, and the remainder titanium.
11. The method of claim 2 , wherein the powdered metal comprises about 6% aluminum, about 4% vanadium, about 0.25% iron, about 0.2% oxygen, and the remainder titanium.
12. The method of claim 1 , wherein the primer insert is about 5 percent to about 30 percent smaller than the primer insert injection mold.
13. The method of claim 1 , wherein the bottom surface comprises a circumferential groove.
14. The method of claim 1 , wherein the flange is a combination of a circumferential groove and one or more notches.
15. The method of claim 1 , wherein the flange comprises one or more notches or scallops positioned circumferential.
16. The method of claim 1 , wherein the flange comprises 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, or 15 notches or scallops positioned circumferential.