FILM LAMINATED, WATER ACTIVATED PAPER TAPE AND METHODS OF MAKING SAME
Water activated tapes, in particular film laminated, water activated paper tapes and methods of making the same are disclosed. The film laminated, water activated paper tapes include a paper backing having a top surface and a bottom surface, a water activated adhesive applied to the bottom surface of the paper backing, and a film reinforcement structure applied to the top surface of the paper backing The film reinforcement structure includes an outermost oriented film, and a lamination layer. The lamination layer may include one or more of an enhanced polyethylene resin, a polyolefin plastomer, a very low density polyethylene, a nylon, a polyester, and a co-polyester laminating the outermost polyolefin film to the paper backing The laminating of the film reinforcement structure to the paper backing is an extrusion lamination process that includes coextruding the outermost polyolefin film and the lamination layer onto the paper backing
1 . A water activated tape comprising:
a paper backing having a top surface and a bottom surface;
a water activated adhesive applied to the bottom surface of the paper backing; and
a film reinforcement structure applied to the top surface of the paper backing, wherein the film reinforcement structure comprises:
an outermost oriented polyolefin film; and
a lamination layer comprising one or more of an enhanced polyethylene resin, a polyolefin plastomer, a very low density polyethylene, a nylon, a polyester, and a co-polyester laminating the outermost polyolefin film to the paper backing.
2 . The water activated tape of claim 1 , wherein the outermost oriented polyolefin film is a biaxially oriented polypropylene film or a biaxially oriented polyethylene terephthalate.
3 . The water activated tape of claim 1 , wherein the outermost polyolefin film has a thickness of about 0.5 mil to about 2 mil.
4 . The water activated tape of claim 3 , wherein the lamination layer has a thickness of about 0.5 mil to about 2 mil.
5 . The water activated tape of claim 4 , wherein the lamination layer has a thickness of about 1 mil to about 1.3 mil.
6 . The water activated tape of claim 1 , wherein the paper backing comprises Kraft paper.
7 . The water activated tape of claim 1 , wherein the lamination layer comprises the enhanced polyethylene resin.
8 . The water activated tape of claim 7 , wherein the lamination layer further comprises a low density polyethylene resin.
9 . The water activated tape of claim 8 , wherein the lamination layer comprises about 40% w/w/to 99% w/w of the enhanced polyethylene resin.
10 . A method of making a film laminated water activated paper tape comprising:
providing a water activated paper tape comprising a paper backing having a water activated adhesive defining a bottom major surface thereof;
extrusion laminating to the paper backing, opposite the water activated adhesive, a film reinforcement structure comprising:
an outermost oriented film; and
an innermost lamination layer comprising one or more of an enhanced polyethylene resin, a polyolefin plastomer, a very low density polyethylene, a nylon, a polyester, and a co-polyester;
wherein the innermost lamination layer is contiguous to the paper backing.
11 . The method of claim 10 , wherein extrusion laminating includes coextruding the outermost polyolefin film and the innermost lamination layer, and thereafter reducing the temperature thereof.
12 . The method of claim 11 , wherein coextruding includes extruding the outermost polyolefin film to have a thickness of about 0.5 mil to about 2.0 mil and extruding the innermost lamination layer to have a thickness of about 0.5 mil to about 2.0 mil.
13 . The method of claim 10 , further comprising providing the paper backing and applying the water activated adhesive to a bottom major surface thereof.
14 . The method of claim 10 , wherein the innermost lamination layer comprises the enhanced polyethylene resin.
15 . The method of claim 10 , wherein the outermost polyolefin film is a biaxially-oriented polypropylene film or a biaxially-oriented polyethylene terephthalate.
16 . The method of claim 14 , wherein the innermost lamination layer is 100% an enhanced polyethylene resin.
17 . The method of claim 10 , wherein the lamination layer comprises about 40% w/w to 99% w/w of the enhanced polyethylene resin.
18 . The method of claim 17 , wherein the lamination layer comprises in balance a low density polyethylene.
19 . The method of claim 17 , wherein the lamination layer further comprises a low density polyethylene.