Low-density molding compound containing surface derivatized microspheres
A molded article is provided that includes a resin matrix having a surface, the resin matrix formed from cross-linked polyester resin or vinyl-ester resin. Microspheroids having a mean diameter of from 16 to 45 microns are embedded in the resin matrix. The microspheroids having a specific gravity of between 0.19 and 0.6 and an isotactic crush strength of greater than or equal to 2750 kilopascals (kPa). Surface activating agent alkoxysilane molecules are covalently bonded to each of the microspheroids. Filler particles are also present in the resin matrix. Fibers are also present in the resin matrix. The fibers being natural fibers, glass fibers, carbon fibers, or a combination thereof. The article has a specific gravity of between 0.80 and 1.25.
1. A molded article comprising:
a resin matrix having a surface;
microspheroids having a mean diameter of from 16 to 45 microns in said resin matrix, said microspheroids consisting of acid cleaned glass microspheroid surfaces to increase the number of the surface activating agent per unit of microspheroid surface area, said microspheroids having a specific gravity of between 0.15 and 0.6 and an isotactic crush strength of greater than or equal to 2750 kilopascals (kPa);
a plurality of surface activating agent molecules covalently bonded to each of said acid cleaned glass microspheroid surfaces _in an amount to form between 0.1 to 1 monolayer on each of said glass microspheroids, said plurality of surface activating agent molecules being alkoxysilanes;
filler particles in said resin matrix; and
fibers in said resin matrix, wherein the article has a specific gravity of between 0.80 and 1.25 and passes a gravel test according to SAE J400.
2. The article of claim 1 further comprising an overcoating layer adhered to the surface, said overcoating layer being commercial paint.
3. The article of claim 1 wherein said microspheroids are present from 10 to 51 total weight percent of the formulation.
4. The article of claim 1 wherein the isotactic crush strength of greater than or equal to 6895 kilopascals (kPa).
5. The article of claim 1 wherein the isotactic crush strength of greater than or equal to 55,158 kilopascals (kPa).
6. The article of claim 1 wherein said plurality of surface activating agent molecules each comprise a moiety that is adapted to covalently bond to said resin matrix.
7. The article of claim 6 wherein said moiety is one of isocyanyl, amino, epoxy, allyl, or methacryl.
8. The article of claim 5 wherein said surface activating agent is a heteroatom functionally terminated thermoplastic coating.
9. The article of claim 8 wherein said coating has a heteroatom containing terminus moiety of: a tertiary amine, a hydroxyl-, an imine- or a cyano-moiety.
10. The article of claim 1 wherein said glass microspheroids have an aspect ratio of normal diameters of between 1.1 and 1.2.
11. The article of claim 1 wherein said resin is a polyester.
12. The article of claim 1 wherein said resin is an epoxy, or a polyurethane.
13. A molded article comprising:
a resin matrix having a surface, said resin matrix formed from cross-linked polyester resin or vinyl-ester resin;
microspheroids having a mean diameter of from 16 to 45 microns in said resin matrix, said microspheroids consisting of acid cleaned glass microspheroid surfaces to increase the number of the surface activating agent per unit of microspheroid surface area, said microspheroids having a specific gravity of between 0.15 and 0.42;
a plurality of surface activating agent molecules covalently bonded to each of said acid cleaned glass microspheroid surfaces in an amount to form between 0.1 to 1 monolayer on each of said glass microspheroids, said plurality of surface activating agent molecules being alkoxysilanes;
filler particles in said resin matrix; and
fibers in said resin matrix, wherein the article has a specific gravity of between 0.80 and 1.25 and passes a gravel test according to SAE J400.
14. The article of claim 13 further comprising an overcoating layer adhered to the surface, said overcoating layer being commercial paint.
15. The article of claim 13 wherein said microspheroids are present from 10 to 51 total weight percent of the formulation.
16. The article of claim 13 wherein the isotactic crush strength of greater than or equal to 6895 kilopascals (kPa).
17. The article of claim 13 wherein the isotactic crush strength of greater than or equal to 55,158 kilopascals (kPa).
18. The article of claim 13 wherein said plurality of surface activating agent molecules each comprise a moiety that is adapted to covalently bond to said resin matrix.
19. The article of claim 18 wherein said moiety is one of isocyanyl, amino, epoxy, allyl, or methacryl.
20. The article of claim 18 wherein said surface activating agent is a heteroatom functionally terminated thermoplastic coating.
21. The article of claim 20 wherein said coating has a heteroatom containing terminus moiety of: a tertiary amine, a hydroxyl-, an imine- or a cyano-moiety.
22. The article of claim 13 wherein said resin is a polyester.
23. The article of claim 1 wherein said resin matrix is formed from cross-linked polyester resin or vinyl-ester resin.
24. The article of claim 1 wherein said microspheroids are present from 12.15 to 20 total weight percent of the formulation.
25. The article of claim 13 wherein said microspheroids are present from 12.15 to 20 total weight percent of the formulation.