Lubricating coating composition and compressor including the same
View Patent ↗A lubricating coating composition and a compressor including a sliding member coated with the lubricating coating composition. The lubricating coating composition includes a thermosetting or thermoplastic polyimide-based resin as a binder, a solid lubricant, various solvents, and other additives at a controlled ratio. The compressor includes a first member including a first sliding surface and a second member moving relative to the first member including a second sliding surface. The lubricating coating composition is applied to the first sliding surface or the second sliding surface.
1. A lubricating coating composition for a surface of an iron based or an aluminum based swash plate, the lubricating coating composition comprising a polyimide-based resin, a solid lubricant, a filler, a silane coupling agent, and a solvent,
wherein based on a total weight of the composition the composition includes about 10 wt % to about 24 wt % of the polyimide-based resin, about 6 wt % to about 10 wt % of the solid lubricant, about 1 wt % to about 2.5 wt % of the filler, about 0.1 wt % to about 2.4 wt % of the coupling agent, and about 60 wt % to about 80 wt % of the solvent, wherein the polyimide-based resin is polyamide imide, the solid lubricant is polytetrafluoroethylene (PTFE), the filler is alumina (Al 2 O 3 ), the coupling agent is Pt(0)-1,3-divinyl-1,1,3,3-tetramethyldisiloxane, the solvent comprises N-methyl-2-pyrrolidone (NMP), xylene, dimethylacetamide (DMAC), and methyl ethyl ketone (MEK), and the lubricating coating composition has a viscosity of about 30 cP to about 40 cP.
2. The lubricating coating composition of claim 1 , wherein the composition comprises the polyimide-based resin and the solid lubricant in a weight ratio of about 1.6:1 to about 3:1.
3. The lubricating coating composition of claim 1 , wherein the solid lubricant has an average particle diameter of about 0.1 to about 1 μm.
4. The lubricating coating composition of claim 1 , wherein the filler has an average particle diameter of about 0 to about 2 μm.
5. The lubricating coating composition of claim 1 , wherein the solvent comprises N-methyl-2-pyrrolidone (NMP) and dimethylacetamide (DMAC) in a weight ratio of about 2.5:1 to about 4:1.