Thin film material for processing use
Provided is a plastic thin film material, on which a process material can be applied or deposited at low cost and with high efficiency, and in which an inorganic substance powder capable of achieving a functional processing for enabling the strong adhesion of a laminated layer on the thin film material is filled at a high density. A thin film material for processing use, which contains a thermoplastic resin and an inorganic substance powder at a weight ratio of 18:82 to 50:50, and has a specific gravity of 0.60 to 1.40 inclusive and a degree of absorption of water of 0.0 to 11.0 g/m 2 ·120 sec inclusive as measured by a Cobb method in accordance with JIS P 8140.
1. A thin monolayer film comprising a thermoplastic resin and an inorganic substance powder at a weight ratio of 18:82 to 50:50, wherein the thin monolayer film comprising the thermoplastic resin and the inorganic substance powder at a weight ratio of 18:82 to 50:50 has each of:
a specific gravity of 0.60 or more and 1.40 or less,
a water absorptiveness as measured by a Cobb method in accordance with JIS P 8140 of 0.0 g/m2·120 sec. or more and 11.0 g/m2·120 sec. or less, and
an air permeance of 800 seconds or more as measured by the Gurley tester method, such that coatability and processability of the thin monolayer film are increased.
2. The thin monolayer film according to claim 1 , wherein the water absorptiveness as measured by the Cobb method is 0.0 g/m2·120 sec. or more and 5.0 g/m2·120 sec. or less.
3. A laminate film having a layer comprising a process material on at least one surface of the thin monolayer film according to claim 1 .
4. A method for manufacturing a laminate film by laminating a process material on at least one surface of the thin monolayer film according to claim 1 .
5. The thin monolayer film according to claim 1 , wherein the contact angle of water on the surface of the thin monolayer film is 40 degrees or more and 90 degrees or less.