View Patent ↗(A) a polymer composition (especially a polyester composition) which includes a compound of tungsten and oxygen (especially tungsten oxide particles) and an additional additive, wherein said additional additive is selected from an acetaldehyde scavenger and a colourant, wherein when said polymer composition includes an acetaldehyde scavenger, said polymer composition includes at least 10 ppm (suitably at least 25 ppm, preferably at least 50 ppm) of said acetaldehyde scavenger and when said polymer composition includes a colourant, said polymer composition includes at least SOpprh (suitably at least 75 ppm, preferably at least 100 ppm) of said colourant, wherein: preferably said article is a preform for a container; or (B) a sheet comprising a polymer composition (especially a polyester, polycarbonate or polyolefin composition) which includes a compound of tungsten and oxygen (especially tungsten oxide particles), wherein said sheet has a width of at least G.3 m.
1. An article comprising:
a polymer composition which includes tungsten oxide particles and an additional additive, wherein said additional additive is selected from an acetaldehyde scavenger and a colourant, wherein when said polymer composition includes an acetaldehyde scavenger, said polymer composition includes at least 10 ppm of said acetaldehyde scavenger and when said polymer composition includes a colourant, said polymer composition includes at least 50 ppm of said colourant, wherein said article is a preform for a container;
wherein said tungsten oxide particles include 18.86 to 20.64 wt % oxygen;
wherein said tungsten oxide particles comprise at least 99 wt % of tungsten and oxygen moieties;
wherein at least 99 wt % of said preform is made up of said polymer composition,
wherein said polymer composition includes at least 99 wt % of a polyester polymer,
wherein said preform has an L* of at least 65,
wherein said tungsten oxide particles have a d50 of less than 25 μm;
wherein said tungsten oxide particles have a span (S) from 0.01 to 5 where S is calculated by the following equation:
S= ( d 90 - d 10 )/ d 50
where d 90 represents a particle size in which 90% of the volume is composed of particles having a smaller diameter than the stated d 90 ; d 10 represents a particle size in which 10% of the volume is composed of particles having a diameter smaller than the stated d 10 ; and d 50 represents a particle size in which 50% of the volume is composed of particles having a diameter larger than the stated d 50 value and 50% of the volume is composed of particles having a diameter smaller than the stated d 50 value; wherein less than 5 vol % of said tungsten oxide particles have a particle size of more than 100 μm; and more than 75 vol % of said tungsten oxide particles have a particle size of more than 0.40 μm.
2. An article according to claim 1 , wherein said tungsten oxide particles include 19.4 to 19.9 wt % oxygen.
3. An article according to claim 1 , said article including 12 to 100 ppm of said tungsten oxide particles.
4. An article according to claim 1 , wherein said tungsten oxide particles have a d 50 of less than 10 μm and greater than 0.1 μm.
5. An article according to claim 1 , wherein said article includes at least 10 ppm and less than 100 ppm of said tungsten oxide particles and the L* is at least 70.
6. An article according to claim 1 , wherein said polyester composition comprises 5 to 150 ppm of tungsten oxide particles, wherein said polyester polymer consists essentially of PET and wherein said tungsten oxide particles include 19. 4 to 19.9 wt % oxygen.
7. An article according to claim 1 , wherein said article includes less than 75 ppm of said tungsten oxide particles.
8. An article according to claim 1 , wherein said article includes 5 to 50 ppm of said tungsten oxide particles.
9. An article according to claim 1 , wherein span (S) is in the range 0.1 to 3.
10. An article according to claim 1 , wherein said tungsten oxide particles have a d50 of at least 0.1 μm.
11. An article according to claim 1 , wherein said tungsten oxide particles have a d50 of less than 2μm.
12. An article according to claim 1 , wherein said article is a preform in the form of a test-tube shaped injection moulding.
13. An article according to claim 1 , wherein said preform has a weight in the range 15 to 40 g and includes 0.00009 g to 0.006 g of said tungsten oxide particles.
14. An article according to claim 1 , wherein:
said tungsten oxide particles include 19.4 to 19.9 wt % oxygen;
said tungsten oxide particles have a d 50 of less than 10 μm and greater than 0.1 μm.
15. An article according to claim 1 , wherein:
said article includes at least 10 ppm and less than 100 ppm of said tungsten oxide particles and the L* is at least 70;
wherein said polyester polymer consists essentially of PET;
wherein said tungsten oxide particles include 19.4 to 19.9 wt % oxygen; said tungsten oxide particles have a d 50 of less than 10 μm and greater than 0.1 μm; and span (S) is in the range 0.1 to 3.
16. An article according to claim 1 , wherein:
said tungsten oxide particles include 19.4 to 19.9 wt % oxygen;
said tungsten oxide particles have a d50 of at least 0.5 μm;
said article is a preform in the form of a test-tube shaped injection moulding; span (S) is in the range 0.1 to 3; and
said preform includes at least 10 ppm and less than 100 ppm of said tungsten oxide particles.
17. An article comprising,
a polymer composition which includes tungsten oxide particles and an additional additive, wherein said additional additive is selected from an acetaldehyde scavenger and a colourant, wherein when said polymer composition includes an acetaldehyde scavenger, said polymer composition includes at least 10ppm of said acetaldehyde scavenger and when said polymer composition includes a colourant, said polymer composition includes at least 50 ppm of said colourant, wherein said article is a preform for a container; wherein said tungsten oxide particles include 18.86 to 20.64 wt % oxygen;
wherein said tungsten oxide particles comprise at least 99 wt % of tungsten and oxygen moieties;
wherein at least 99 wt % of said preform is made up of said polymer composition,
wherein said polymer composition includes at least 99 wt % of a polyester polymer,
wherein said preform has an L* of at least 65,
wherein said tungsten oxide particles have a d50 of less than 25 μm;
wherein said tungsten oxide particles have a span (S) from 0.01 to 5 where S is calculated by the following equation:
S= ( d 90 - d 10 )/ d 50
where d 90 represents a particle size in which 90% of the volume is composed of particles having a smaller diameter than the stated d 90 ; d 10 represents a particle size in which 10% of the volume is composed of particles having a diameter smaller than the stated d 10 ; and d 50 represents a particle size in which 50% of the volume is composed of particles having a diameter larger than the stated d 50 value and 50% of the volume is composed of particles having a diameter smaller than the stated d 50 value wherein said article includes 50 ppm or less of said tungsten oxide particles; and
wherein said tungsten oxide particles have a d 50 of less than 10 μm and greater than 0.1 μm.
18. An article according to claim 17 , wherein less than 5 vol % of said tungsten oxide particles have a particle size of more than 100 μm; and more than 75 vol % of said tungsten oxide particles have a particle size of more than 0.40 μm.
19. An article comprising a polymer composition which includes tungsten oxide particles and an additional additive, wherein said additional additive is selected from an acetaldehyde scavenger and a colourant, wherein when said polymer composition includes an acetaldehyde scavenger, said polymer composition includes at least 10 ppm of said acetaldehyde scavenger and when said polymer composition includes a colourant, said polymer composition includes at least 50 ppm of said colourant, wherein said article is a preform for a container;
wherein said tungsten oxide particles include 18.86 to 20.64 wt % oxygen;
wherein said tungsten oxide particles comprise at least 99 wt % tungsten and oxygen moieties;
wherein at least 99 wt % of said preform is made up of said polymer composition,
wherein said polymer composition includes at least 99 wt % of a polyester polymer,
wherein said preform has an L* of at least 65,
wherein said tungsten oxide particles have a d50 of less than 25 μm;
wherein said tungsten oxide particles have a span (S) from 0.01 to 5 where S is calculated by the following equation:
S= ( d 90 - d 10 )/ d 50
where d 90 represents a particle size in which 90% of the volume is composed of particles having a smaller diameter than the stated d 90 d 10 represents a particle size in which 10% of the volume is composed of particles having a diameter smaller than the stated d 10 ; and d 50 represents a particle size in which 50% of the volume is composed of particles having a diameter larger than the stated d 50 value and 50% of the volume is composed of particles having a diameter smaller than the stated d 50 value, wherein said tungsten oxide particles have a d50 of at least 0.5 μm.