Coated luminescent particle, a luminescent converter element, a light source, a luminaire and a method of manufacturing a coated luminescent particle

1. A coated luminescent particle, the coated luminescent particle comprising:

a luminescent particle of a luminescent material, the luminescent material being configured to absorb light in a first spectral range and to convert a portion of the absorbed light towards light of a second spectral range,

a first coating layer formed using layer deposition techniques forming a first barrier, first barrier being a water barrier, the first coating layer selected from the group of a metal oxide, a nitride, a phosphide and a sulfide-based coating, a thickness (th 1 ) of the first coating layer is 5 nm≤th 1 ≤30 nm, and

a second coating layer formed using a sol-gel process forming a second barrier, second barrier being a water barrier, the second coating layer comprising a silicon-based polymer, a thickness (th 2 ) of the second coating layer is 30 nm≤th 2 ≤80 nm,

the first coating layer and the second coating layer are light transmitting,

the first coating layer encapsulates the luminescent particle and the second coating layer encapsulates the first coating layer.

2. The coated luminescent particle according to claim 1 , wherein the luminescent material comprises sulfide and/or selenide, or a luminescent material of the groups of orthosilicates or thiogallates.

3. The coated luminescent particle according to claim 1 , wherein the luminescent material comprises at least one of the materials calcium sulfide, strontium sulfide, calcium selenide sulfide.

4. The coated luminescent particle according to claim 1 , wherein a diameter of the luminescent particle is smaller than 200 micrometer.

5. The coated luminescent particle according to claim 1 , further comprising a third coating layer being interposed between the first coating layer and the second coating layer, the third coating layer is selected from the group consisting of a metal oxide layer and a layer of a silicon based polymer, wherein the third coating layer is light transmitting and forms a barrier for water.

6. The coated luminescent particle according to claim 1 , wherein the silicon based polymer is obtained from a material from a group of compounds formed by

wherein R 1 , R 2 , and R 3 are hydrolysable alkoxy groups and R 4 is selected from the group consisting of C1-C6 linear alkyl groups, hydrolysable alkoxy groups and a phenyl group.

7. The coated luminescent particle according to claim 6 , wherein the silicone-based polymer is obtained from a material from the group of tetramethoxysilane and tetraethoxysilane.

8. A luminescent converter element comprising:

coated luminescent particles according to claim 1 , and

a binder for binding the coated luminescent particles in the luminescent converter element.

9. A light source comprising:

a light emitter for emitting a light emission, the light emission comprising light in the first spectral range,

a luminescent converter element according to claim 8 , the luminescent converter element arranged to receive light being emitted by the light emitter.

10. The coated luminescent particle according to claim 1 further comprising a third coating layer being interposed between the first coating layer and the second coating layer, wherein the third coating layer is a continuous layer of a third material, the third material selected from the group consisting of AlPO 4 , SiO 2 , Al 2 O 3 , and LaPO 4 , wherein the third coating layer is light transmitting and forms a water barrier.

11. The coated luminescent particle according to claim 1 , wherein the silicon based polymer is obtained from a material from a group of compounds formed by

wherein R 1 , R 2 , and R 3 are individually selected from the group consisting of —OCH 3 and —OC 2 H 5 and R4 is selected from the group consisting of —OCH 3 and —OC 2 H 5 .

12. A light source comprising:

a light emitter for emitting a light emission, the light emission comprising light in the first spectral range,

a plurality of coated luminescent particles according to claim 1 , the coated luminescent particles being arranged to receive light being emitted by the light emitter.

13. A method of manufacturing coated luminescent particles, the method comprising:

providing luminescent particles of a luminescent material, the luminescent particles being configured to absorb light in a first spectral range and to convert a portion of the absorbed light towards light of a second spectral range,

depositing a first light transmitting coating layer using layer deposition techniques to form a first water barrier that encapsulates the luminescent particle, the first coating layer selected from the group of a metal oxide, a nitride, a phosphide and a sulfide-based coating, a thickness (th 1 ) of the first coating layer is 5 nm≤th 1 ≤30 nm, and

depositing a second light transmitting coating layer using a sol-gel process to form a second water barrier that encapsulates the first coating layer, the second coating layer comprising a silicon-based polymer, a thickness (th 2 ) of the second coating layer is 30 nm≤th 2 ≤80 nm.

14. The method of manufacturing coating luminescent particles according to claim 13 , wherein the stage of manufacturing the second coating layer comprises the stage of obtaining a solution of a first material in water, wherein the first material is one of a group of compounds formed by

wherein R1, R2 and R3 are hydrolysable alkoxy groups and R4 is selected from the group consisting of C1-C6 linear alkyl groups, hydrolysable alkoxy groups and a phenyl group, or

R1, R2 and R3 are individually selected from —OCH 3 and —OC 2 H 5 and R4 is selected from —OCH 3 and —OC 2 H 5 .