Thermoset polyol compositions and methods of use thereof
View Patent ↗A molding composition formulation is provided of a thermoset cross-linkable polyol having unsaturated backbone comprising the structure defined by formula 1: (1) a reinforcing filler; and optionally, a flame retardant, a UV stabilizer or a composition comprising one of the foregoing.
1. A molding composition formulation comprising: a thermoset cross-linkable polyol resin having an unsaturated backbone comprising the structure defined by formula 1:
where A is a saturated or unsaturated aliphatic C 1-18 chain, —(CH2) m —C(OH)—, or a composition comprising at least one of the foregoing;
R and R 2 are each independently, a saturated or unsaturated aliphatic, or cycloaliphatic polymer, an aliphatic or cycloaliphatic alcohol, cyanate, or a composition comprising at least one of the foregoing; R 1 is H, C 1-18 chain, or a composition comprising at least one of the foregoing; and n is an integer between 1 and 500;
a reinforcing filler; and
optionally, a flame retardant, a UV stabilizer or a composition comprising one of the foregoing.
2. The composition of claim 1 , wherein the thermoset cross-linkable polyol comprises polyether diol or poly triol with number average molecular weight of 200 to 2000.
3. The composition of claim 1 , wherein the thermoset cross-linkable polyol comprises a polyester polyol.
4. The composition of claim 1 , wherein R 1 is polypropylene oxide.
5. The composition of claim 1 , wherein A comprises polytetramethylene glycol.
6. The composition of claim 1 , wherein A comprises a polyether.
7. The composition of claim 1 , further comprising: a thickener system comprising a polyether amine and an isocyanate.
8. The composition of claim 1 , wherein R 1 is hydrogen and wherein the ratio of hydroxyl groups to carboxyl groups is between about 0.33 and 6.0.
9. The composition of claim 1 , wherein the reinforcing fiber is a discontinuous fiber having a fiber length of about 3 mm to 50 mm.
10. The composition of claim 9 , wherein the discontinuous fiber is carbon, glass, aramid, polypropylene, polyethyelene, basalt, poly{diimidazo pyridinylene (dihydroxy) phenylene} fiber or a fiber composition comprising at least one of the foregoing.
11. The composition of claim 1 , further comprising a cross-linking agent.
12. The composition of claim 11 , wherein the cross-linking agent is poly(isocyanate), a monomeric dihydroxy-terminated compound, a low-molecular weight poly(amine), or a telechelic composition comprising at least one of the foregoing.
13. The composition of claim 12 , wherein the monomeric dihydroxy-terminated compound is propylene glycol, ethylene glycol, 1,2-butane diol, 1,4-butane diol, or a composition comprising at least one of the foregoing.
14. The composition of claim 1 , further comprising a non-fibrous filler.
15. The composition of claim 14 , wherein the non-fibrous filler is calcium carbonate, alumnina, clay, mica, wollastonite, silicate, magnesium oxide, wood flour, and mixtures thereof, wherein the non-fibrous filler has a particle size d 3,2 of between 0.02 to 6.00 μm.
16. A molded article of manufacture comprising the composition of claim 1 in a cured state corresponding a shape of a mold.