Polymer material for highly efficient organic thin-film solar cell, and organic thin-film solar cell using same
View Patent ↗The present invention relates to a novel polymeric material for a highly efficient organic thin-film solar cell with high hole mobility and power conversion efficiency. In the polymeric material, a compound containing an electron donating group represented by Formula 1 or 2 and a compound containing an electron accepting group represented by one of Formulae 3 to 8 are repeatedly introduced in an alternating manner.
1. A polymer in which a compound containing an electron donating group represented by Formula 1 or 2:
(wherein the moieties X are the same or different and each represents CRR′, NR, O, SiRR′, PR, S, GeRR′, Se or Te; R and R′ are the same or different and each represents a C 1 -C 30 linear or branched alkyl group; R 1 , R 2 , R 3 , and R 4 are the same or different and each represents a C 8 -C 30 linear or branched alkyl group; and the subscripts n are the same or different and each represents an integer from 1 to 3), and a compound containing an electron accepting group represented by one of Formulae 3 to 8:
(wherein X, R, and R′ are as defined in Formula 1 or 2; the groups Y are the same or different and each represents H, F, Cl or CN; and R 5 , R 6 , R 7 , R 8 , R 9 , R 10 , R 11 , and R 12 are the same or different and each represents a C 8 -C 30 linear or branched alkyl group) are repeatedly introduced in an alternating manner.
2. The polymer according to claim 1 , wherein the compound containing an electron donating group is represented by Formula 1 and the compound containing an electron accepting group is represented by Formula 3.
3. The polymer according to claim 1 , wherein the polymer is selected from compounds represented by Formulae 9 to 11:
wherein each n is independently an integer from 1 to 3, each m is independently an integer from 10 to 100, and R 13 , R 14 , R 15 , R 16 , R 17 , and R 18 are the same or different and each represents a C 8 -C 30 linear or branched alkyl group.
4. The polymer according to claim 1 , wherein the polymer has a number average molecular weight of 10,000 g/mol to 100,000 g/mol.
5. A method for fabricating an organic thin-film solar cell, comprising forming a sunlight-absorbing photoactive layer comprising the polymer according to claim 1 by the use of chlorobenzene as a solvent and the addition of diphenyl ether as an additive.
6. An organic thin-film solar cell comprising a sunlight-absorbing photoactive layer comprising the polymer according to claim 1 .
7. The organic thin-film solar cell according to claim 6 , wherein the organic thin-film solar cell is fabricated by the method according to claim 5 .
8. The organic thin-film solar cell according to claim 6 , further comprising a buffer layer formed between a cathode layer and the sunlight-absorbing photoactive layer and comprising a poly(fluorene-phenylene)-based conjugated polymer electrolyte (CPE).
9. The organic thin-film solar cell according to claim 8 , wherein the conjugated polymer electrolyte is poly[9,9-bis(6′-(N,N,N-trimethylammonium)hexyl)fluorene-alt-phenylene]with bromide (PAHFP-Br).
10. An organic thin-film transistor comprising the polymer according to claim 1 as an active material.