Manufacturing method of press-formed member and press forming apparatus
View Patent ↗In a press forming step of obtaining, from a blank of high-tensile strength steel sheet of 390 MPa or more, a press-formed product with a shape of cross section having a groove bottom part, ridge line parts, and vertical wall parts. An outward flange including parts along the ridge line parts is formed at an end part in a longitudinal direction. Forming parts to the ridge line parts is started by creating a region positioned at an end portion, in a longitudinal direction, of a part to be formed to the groove bottom part of the blank, which is separated from a punch top part. At that time or thereafter, the region is made to approach the punch top part. When forming the ridge line parts, forming of the parts of the outward flange are conducted, the parts are formed from the start to the middle of the press forming, to reduce or prevent an occurrence of stretch flange fracture and a generation of wrinkling
1. A manufacturing method of a press-formed member, comprising
a press forming step of obtaining, from a blank of high-tensile strength steel sheet of 390MPa or more, a press-formed product with a shape of cross section having at least a groove bottom part, a ridge line part continued to an end portion in a width direction of the groove bottom part, and a vertical wall part continued to the ridge line part, and in which an outward flange including a part along the ridge line part is formed at an end part in a longitudinal direction, by using a press forming apparatus including a punch and a die, wherein
the press forming step includes:
creating a state where a radius of curvature r p of a part to be formed to the ridge line part of the blank once becomes larger than a radius of curvature r f of the ridge line part at a point of time of completion of the press forming, in the middle of the press forming;
making the radius of curvature r p approach the radius of curvature r f in a process of the press forming thereafter; and
completing, when the press forming is completed, the forming of the groove bottom part, the forming of the ridge line part, the forming of the vertical wall part, and the forming of the outward flange.
2. The manufacturing method of the press-formed member according to claim 1 , wherein
in the state where the radius of curvature r p becomes larger than the radius of curvature r f , a region in which the curvature is formed is in a state of being wider than a region of the ridge line part at the point of time of completion of the press forming, and is in a state of being widened by being extended toward the groove bottom part side.
3. A manufacturing method of a press-formed member, comprising
a press forming step of obtaining, from a blank of high-tensile strength steel sheet of 390 MPa or more, a press-formed product with a shape of cross section having at least a groove bottom part, a ridge line part continued to an end portion in a width direction of the groove bottom part, and a vertical wall part continued to the ridge line part, and in which an outward flange including a part along the ridge line part is formed at an end part in a longitudinal direction, by using a press forming apparatus including a punch and a die, wherein
the press forming step includes:
a first step of starting forming of a part to be formed to the ridge line part and forming of the outward flange, by creating a state where a region positioned at least at an end portion in a longitudinal direction of a part to be formed to the groove bottom part of the blank is separated from a punch top part, in the punch, which forms the groove bottom part;
a second step of making, at the time of starting the forming of the part to be formed to the ridge line part or thereafter, the region approach the punch top part; and
completing, when the press forming is completed, the forming of the groove bottom part, the forming of the ridge line part, the forming of the vertical wall part, and the forming of the outward flange.
4. The manufacturing method of the press-formed member according to claim 3 , wherein:
in the first step, the region is set to be in the state of being separated from the punch top part by creating a state where a first pad provided to be able to freely protrude from or withdraw into the punch top part, is protruded from the punch top part; and
in the second step, the first pad is lowered to make the region approach the punch top part.
5. The manufacturing method of the press-formed member according to claim 4 , wherein
the first pad and a second pad provided on a side opposite to that of the first pad with the blank provided therebetween are used to sandwich and bind the blank.
6. The manufacturing method of the press-formed member according to claim 5 , further comprising
a post-press forming step with respect to the press-formed product, wherein
in the post-press forming step, the outward flange of the press-formed product is further raised.
7. The manufacturing method of the press-formed member according to claim 4 , further comprising
a post-press forming step with respect to the press-formed product, wherein
in the post-press forming step, the outward flange of the press-formed product is further raised.
8. The manufacturing method of the press-formed member according to claim 3 , further comprising
a post-press forming step with respect to the press-formed product, wherein
in the post-press forming step, the outward flange of the press-formed product is further raised.