Method for producing activated carbon sheet and method for improving impregnation of activated carbon sheet with electrolyte solution
A method for producing an activated carbon sheet having high electrolyte impregnation capacity and high mechanical strength is provided. The method for producing an activated carbon sheet includes a sheet preparation step of preparing a sheet including an activated carbon, an electrically conductive carbon material, and a fibrous fluorocarbon resin binder, which fluorocarbon resin is polytetrafluoroethylene and/or modified polytetrafluoroethylene; and a light irradiation step of performing light irradiation of at least one side of the sheet such that the cumulative irradiation dose on the sheet surface is 50 to 1000 mJ/cm 2 .
1. A method for producing an activated carbon sheet, said method comprising:
preparing a sheet comprising an activated carbon, an electrically conductive carbon material, and a fibrous fluorocarbon resin binder, wherein said fluorocarbon resin is at least one resin selected from the group consisting of polytetrafluoroethylene and a modified polytetrafluoroethylene obtained by copolymerization of tetrafluoroethylene and one or more other kind of monomer; and
performing light irradiation of at least one side of said sheet such that the cumulative irradiation dose on the sheet surface is 130 to 1000 mJ/cm 2 .
2. The method for producing an activated carbon sheet according to claim 1 , wherein said light irradiation is ultraviolet irradiation by an excimer lamp in the presence of oxygen gas and/or ozone gas.
3. The method for producing an activated carbon sheet according to claim 2 , wherein said activated carbon sheet is an electrode for an electric double layer capacitor.
4. The method for producing an activated carbon sheet according to claim 1 , wherein said activated carbon sheet is an electrode for an electric double layer capacitor.
5. The method for producing an activated carbon sheet according to claim 1 , wherein said light irradiation is performed in the presence of oxygen gas and/or ozone gas.
6. The method for producing an activated carbon sheet according to claim 5 , wherein said light irradiation is performed in the presence of oxygen gas.
7. A method for improving the electrolyte impregnation capacity of an activated carbon sheet, said method comprising:
performing light irradiation of at least one side of an activated carbon sheet comprising an activated carbon, an electrically conductive carbon material, and a fibrous fluorocarbon resin binder, said fluorocarbon resin is at least one resin selected from the group consisting of polytetrafluoroethylene and a modified polytetrafluoroethylene obtained by copolymerization of tetrafluoroethylene and one or more other kind of monomer, such that the cumulative irradiation dose on the sheet surface is 130 to 1000 mJ/cm 2 .
8. The method for improving the electrolyte impregnation capacity of an activated carbon sheet according to claim 7 , wherein said light irradiation is ultraviolet irradiation by an excimer lamp in the presence of oxygen gas and/or ozone gas.
9. The method for improving the electrolyte impregnation capacity of an activated carbon sheet according to claim 8 , wherein said activated carbon sheet is an electrode for an electric double layer capacitor.
10. The method for improving the electrolyte impregnation capacity of an activated carbon sheet according to claim 7 , wherein said activated carbon sheet is an electrode for an electric double layer capacitor.
11. The method for improving the electrolyte impregnation capacity of an activated carbon sheet according to claim 7 , wherein said light irradiation is performed in the presence of oxygen gas and/or ozone gas.
12. The method for improving the electrolyte impregnation capacity of an activated carbon sheet according to claim 11 , wherein said light irradiation is performed in the presence of oxygen gas.