Method for removing rare earth impurities from nickel-electroplating solution
A method for removing rare earth impurities from a nickel-electroplating solution by adding a rare earth compound to the nickel-electroplating solution containing rare earth impurities, keeping the electroplating solution at 60° C. or higher for a certain period of time, and then removing precipitate generated by the heating from the nickel-electroplating solution together with the added rare earth compound by sedimentation and/or filtration.
1. A method for removing rare earth impurities from a nickel-electroplating solution, consisting essentially of
adding a rare earth compound to said nickel-electroplating solution containing rare earth impurities;
keeping said nickel-electroplating solution at 60° C. or higher for 6 hours or more such that some components in the nickel-electroplating solution are not precipitated, and then
removing a precipitate of the rare earth impurities generated by said heating from said nickel-electroplating solution together with the added rare earth compound by sedimentation and/or filtration.
2. The method for removing rare earth impurities from a nickel-electroplating solution according to claim 1 , wherein said rare earth compound is rare earth oxide.
3. The method for removing rare earth impurities from a nickel-electroplating solution according to claim 1 , wherein a rare earth element constituting said rare earth compound is neodymium.
4. The method for removing rare earth impurities from a nickel-electroplating solution according to claim 1 , wherein said nickel-electroplating solution is stirred while heating.
5. The method for removing rare earth impurities from a nickel-electroplating solution according to claim 4 , wherein the stirring of the solution is achieved by air, rotating stirring blades, or circulation by a pump.
6. The method for removing rare earth impurities from a nickel-electroplating solution according to claim 1 , wherein the adding is by adding the rare earth compound in the form of powder, or after being stirred in water, or by adding the rare earth compound to an aqueous acid solution which is then charged into the nickel-electroplating solution.
7. The method for removing rare earth impurities from a nickel-electroplating solution according to claim 1 , wherein the rare earth compound is at least one selected from a rare earth oxide, a rare earth hydroxide, a rare earth salt and a rare earth sulfate.