A method for forming a beverage can end ( 34 a ) having ink jet markings ( 50 a ) on its tab ( 36 a ) comprises a step of applying ink via an ink jet to a surface of tab stock, wherein the tab stock surface is unlubricated and substantially free of factory lubricant. The method further includes a step of lubricating the tab stock after the step of applying ink, a step of forming the tab stock into tabs, and a step of combining the tabs with an end shell to from the beverage can end.
1. A method for forming a beverage can end having ink jet markings on its tab, comprising the steps of:
treating a tab stock with a solvent to remove factory lubricant;
after the step of treating the tab stock, feeding the tab stock into a printing station without coiling the tab stock;
at the printing station applying ink via an ink jet to a surface of the tab stock, the tab stock surface being unlubricated and substantially free of factory lubricant;
after the step of applying ink, feeding the tab stock via a lubrication station directly into a tab press without coiling the tab stock, where the printing station, the lubrication station, and the tab press belong to a system;
forming the tab stock into tabs in the tab press; and
combining the tabs with an end shell to form the beverage can end.
2. The method of claim 1 further comprising a step of uncoiling the tab stock, wherein the applying step is performed after the uncoiling step.
3. The method of claim 1 wherein the applying step is performed on an underside of the tab stock.
4. The method of claim 1 wherein the applying step is performed on top side of the tab stock.
5. The method of claim 1 wherein the applying step includes applying indicia to the tab stock.
6. The method of claim 1 wherein the factory lubricant is DOS and the solvent is configured to remove DOS from the tab stock surface.
7. The method of claim 6 wherein, before the applying step, the tab stock has a surface energy of between 36 dyn/cm and 44 dyn/cm on a surface tension test.
8. The method of claim 6 wherein, before the applying step, the tab stock has a surface energy of less than 42 dyn/cm on a surface tension test.
9. The method of claim 6 wherein, before the applying step, the tab stock has a surface energy of less than 40 dyn/cm on a surface tension test.
10. The method of claim 6 wherein, before the applying step, the tab stock has a surface energy of less than 38 dyn/cm on a surface tension test.
11. The method step of claim 1 further comprising steps of receiving the tab stock; and cleaning factory lubricant from the tab stock.
12. The method step of claim 1 further comprising a step of increasing the surface energy of the tab stock.
13. The method of claim 1 , wherein the factory lubricant includes DOS, and wherein the tab stock is suitable for being formed into beverage or food can tabs.
14. The method of claim 1 , wherein the method for forming the beverage can end is performed at line speeds of over 400 strokes per minute.
15. The method of claim 14 , wherein the tab stock includes at least a two tab width stock.
16. The method of claim 2 , wherein the treating step is performed after the uncoiling step.