Method for producing graphite and particulates for graphite production
View Patent ↗Provided are a method for producing artificial graphite through a vertical graphitization furnace with easy circulation of inert gas, uniform heating and no damage to the furnace; and particulates used therefor. The method comprises steps of: introducing graphitizable particulates having average particle diameter of 3 to 30 mm into an inside of the furnace from upper part thereof, heating the particulates at 2200° C. to 3200° C. while making inert gas flow from lower part toward upper part thereof to graphitize the particulates, and removing the graphite through lower part thereof. The particulates have average particle diameter of 3 to 30 mm and are obtained by granulating mixture comprising 100 wt parts of graphitizable carbonaceous substance powder having average particle diameter of 10 to 20 μm, 3 to 20 wt parts of binder decomposable at lower than 1000° C., and 5 to 30 wt parts of liquid which can dissolve the binder.
1. A method for producing graphite, comprising the steps of:
introducing graphitizable material particulates having an average particle diameter of 3 to 30 mm into an inside of a vertical graphitization furnace from an upper part thereof,
heating the graphitizable material particulates at 2200° C. to 3200° C. while making inert gas flow from a lower part toward an upper part thereof to graphitize the graphitizable material particulates, and
removing obtained graphite through a lower part thereof,
wherein the graphitizable material particulates are obtained by granulating a mixture comprising 100 parts by weight of graphitizable carbonaceous substance powder having an average particle diameter of 10 to 20 μm, 3 to 20 parts by weight of a binder evaporable or evaporable through decomposition at a temperature of lower than 1000° C., and 5 to 30 parts by weight of a solvent or a dispersant which can dissolve or disperse the binder.
2. The method for producing graphite according to claim 1 , wherein the binder is a water-soluble polymer and the solvent is water.
3. The method for producing graphite according to claim 1 , further comprising a step of crushing the graphite removed through the lower part of the vertical graphitization furnace to obtain a graphite powder.
4. Particulates for use in producing graphite through a vertical graphitization furnace, the particulates having an average particle diameter of 3 to 30 mm and being obtained by granulating a mixture comprising 100 parts by weight of graphitizable carbonaceous substance powder having an average particle diameter of 10 to 20 μm, 3 to 20 parts by weight of a binder evaporable or evaporable through decomposition at a temperature of lower than 1000° C., and 5 to 30 parts by weight of a solvent or a dispersant which can dissolve or disperse the binder.