Low-oxygen clean steel and low-oxygen clean steel product

1. A low-oxygen clean steel containing C, Si, Mn, P, and S as chemical components, and further containing, by mass %, 0.010% to 0.20% of Al, 0.0001% to 0.0003% of Ca, 0.00005% to 0.0004% of REM, and greater than 0% to 0.003% of T.O,

wherein the REM content, the Ca content, and the T.O content satisfy the following Expressions 1 and 2,

nonmetallic inclusions which have a maximum predicted diameter of 1 μm to 30 μm measured using an extreme value statistical method under the condition in which a prediction area is 30,000 mm 2 , and contain Al 2 O 3 and REM oxide are dispersed in the steel,

a proportion of the Al 2 O 3 is greater than 50% by mass based on the total amount of nonmetallic inclusions,

a proportion of CaO is 1.0% or less by mass based on the total amount of the nonmetallic inclusions,

the REM is one or two or more of rare-earth elements La, Ce, Pr, and Nd, and

the steel is Al-deoxidized steel or Al—Si-deoxidized steel,

0.15≤REM/Ca≤4.00  Expression 1,

Ca/T.O≤0.50  Expression 2.

2. The low-oxygen clean steel according to claim 1 ,

wherein the following Expression 3 is satisfied,

0.05≤REM/T.O≤0.50  Expression 3.

3. The low-oxygen clean steel according to claim 1 , containing, by mass %, 1.20% or less of C, 3.00% or less of Si, 16.0% or less of Mn, 0.05% or less of P, and 0.05% or less of S as the chemical components with the remainder Fe and impurities.

4. The low-oxygen clean steel according to claim 3 , further containing, by mass %, one or two or more of 3.50% or less of Cr, 0.85% or less of Mo, 4.50% or less of Ni, 0.20% or less of Nb, 0.45% or less of V, 0.30% or less of W, 0.006% or less of B, 0.06% or less of N, 0.25% or less of Ti, 0.50% or less of Cu, 0.45% or less of Pb, 0.20% or less of Bi, 0.01% or less of Te, 0.20% or less of Sb, and 0.01% or less of Mg as the chemical components.

5. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 1 .

6. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 3 .

7. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 4 .

8. The low-oxygen clean steel according to claim 2 , containing, by mass %, 1.20% or less of C, 3.00% or less of Si, 16.0% or less of Mn, 0.05% or less of P, and 0.05% or less of S as the chemical components with the remainder Fe and impurities.

9. The low-oxygen clean steel according to claim 8 , further containing, by mass %, one or two or more of 3.50% or less of Cr, 0.85% or less of Mo, 4.50% or less of Ni, 0.20% or less of Nb, 0.45% or less of V, 0.30% or less of W, 0.006% or less of B, 0.06% or less of N, 0.25% or less of Ti, 0.50% or less of Cu, 0.45% or less of Pb, 0.20% or less of Bi, 0.01% or less of Te, 0.20% or less of Sb, and 0.01% or less of Mg as the chemical components.

10. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 2 .

11. A low-oxygen clean steel product produced by processing the low-oxygen clean steel according to claim 8 .

12. The low-oxygen clean steel according to claim 1 , wherein a proportion of SiO 2 in the inclusions is 1.0% or less by mass based on the total amount of nonmetallic inclusions.

13. The low-oxygen clean steel according to claim 1 , wherein the proportion of the Al 2 O 3 in the inclusions is greater than 61.8% to 82.9% by mass based on the total amount of the nonmetallic inclusions.

14. The low-oxygen clean steel according to claim 1 , wherein the proportion of the Al 2 O 3 is greater than 66.0% to 82.9% by mass based on the total amount of nonmetallic inclusions.